Study of fatigue life and filler interaction of paper sludge filled epoxidized natural rubber (ENR) and maleated natural rubber (MNR) composites

An investigation on the effect of epoxidation and maleated natural rubber (MNR) on fatigue and rubber-filler interaction properties of paper sludge filled natural rubber composites was elucidated. Paper sludge loading was varied from 0 to 40 phr and conventional vulcanisation system was used while compounding was carried out on a laboratory sized two roll mill. Two different types of natural rubber, SMR L and ENR 50 having 0 and 50 mole% of epoxidation were used in order to investigate the effect of epoxidation on the composites. Results indicate that, at a fixed filler loading, ENR 50 vulcanizates exhibit higher fatigue life than SMR L vulcanizates especially at filler loading below 20 phr which might be associated with better rubber-filler interaction. In the case of composites with the addition of maleated natural rubber (MNR), a higher fatigue life was observed due to presence of physical and/or chemical linkages, which increases the interfacial adhesion. Scanning electron microscopy (SEM) micrographs of fatigue fracture surfaces and rubber-filler interaction study supported the observed result on fatigue life.