Spectroscopic interpretation for Na-induced phase transitions on Na/Si(111)3 x 1

Na adsorption at room temperature causes the Na/Si(111)3 x 1 surface with Na coverage of 1/3 monolayer (ML) to transit into the Na/Si(111)6 x 1 surface at 1/2 ML and sequentially into the Na/Si(111)3 x 1 surface at 2/3 ML. The phase transition was studied by Si 2p core-level photoemission spectroscopy. The detailed line shape analysis of the Si 2p core-level spectrum of the Na/Si(111)3 x 1 surface (2/3 ML) is presented and compared to the Na/Si(111)3 x 1 surface (1/3 ML) which is composed of Si honeycomb chain-channel structures. This suggests that as additional Na atoms form atomic chains resulting in the Na/Si(111)3 x 1 surface (2/3 ML), the inner atoms of the Si honeycomb chain-channel structure is buckled due to the additional Na atoms. (c) 2006 Elsevier B.V. All rights reserved.