Room-temperature deformation behavior of directionally solidified multiphase Ni-Fe-Al alloys

被引:53
|
作者
Misra, A [1 ]
Gibala, R [1 ]
机构
[1] UNIV MICHIGAN,DEPT MAT SCI & ENGN,ANN ARBOR,MI 48109
来源
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 1997年 / 28卷 / 3A期
基金
美国国家科学基金会;
关键词
D O I
10.1007/s11661-997-1007-4
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Directionally solidified (DS) beta + (gamma + gamma') Ni-Fe-Al alloys have been used to investigate the effect of a ductile second phase on the room-temperature mechanical behavior of a brittle [001]-oriented beta (B2) phase. The ductile phase in the composite consisted of a fine distribution of-ordered gamma' precipitates in a gamma (fcc) matrix. Three microstructures were studied: 100 pct lamellar/rod, lamellar + proeutectic beta, and discontinuous gamma. The beta matrix in the latter two microstructures contained fine-scale bcc precipitates formed due to spinodal decomposition. Room-temperature tensile ductilities as high as 12 pct and fracture toughness (K-Q) of 30.4 MPa root m were observed in the 100 pct lamellar/rod microstructure. Observations of slip traces and dislocation substructures indicated that a substantial portion of the ductility was a result of slip transfer from the ductile phase to the brittle matrix. This slip transfer was facilitated by the Kurdjumov-Sachs (KS) orientation relationship between the two phases and the strong interphase interface which showed no decohesion during deformation. In microstructures which show higher values of tensile ductility and fracture toughness, [100] slip was seen in the beta phase, whereas [111] slip was seen in the beta phase in the microstructure which showed limited ductility. The high ductility and toughness are explained:in terms of increased nobile dislocation density afforded by interface constraint. The effect of extrinsic toughening mechanisms on enhancing the ductility or toughness is secondary to that of slip transfer.
引用
收藏
页码:795 / 807
页数:13
相关论文
共 50 条
  • [41] High temperature cyclic deformation of a directionally solidified Ni-base superalloy
    Marchionni, M.
    Osinkolu, G.A.
    Maldini, M.
    Fatigue and Fracture of Engineering Materials and Structures, 1996, 19 (08): : 955 - 962
  • [42] DEFORMATION TWINNING IN AUSTENITE FE-NI-C ALLOYS AT ROOM TEMPERATURE
    KOUNICKY, J
    PHILOSOPHICAL MAGAZINE, 1968, 18 (151): : 205 - &
  • [43] Tensile property and deformation behavior of a directionally solidified Ni-base superalloy
    Chu, Zhaokuang
    Yu, Jinjiang
    Sun, Xiaofeng
    Guan, Hengrong
    Hu, Zhuangqi
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 527 (12): : 3010 - 3014
  • [44] High temperature cyclic deformation of a directionally solidified Ni-base superalloy
    Marchionni, M
    Osinkolu, GA
    Maldini, M
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1996, 19 (08) : 955 - 962
  • [45] Microstructure and room-temperature fracture toughness of directionally solidified Nb-Si-Ti-Cr-Al-Hf alloy
    Su, Linfen
    Jia, Lina
    Feng, Yubei
    Zhang, Huarui
    Yuan, Sainan
    Zhang, Hu
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2013, 560 : 672 - 677
  • [46] HIGH-TEMPERATURE (111) SLIP BEHAVIOR OF A DIRECTIONALLY SOLIDIFIED NI3AL ALLOY
    LIN, DL
    ZHANG, Y
    LIN, H
    HIGH TEMPERATURE MATERIALS AND PROCESSES, 1995, 14 (03) : 137 - 149
  • [47] Room-temperature tensile properties of a directionally solidified magnesium alloy and its deformation mechanism dominated by contraction twin and double twin
    Lin, Xiao-ping
    Zhao, Tian-bo
    Dong, Yun
    Ye, Jie
    Fan, Zhi-bin
    Xie, Hong-bin
    Wang, Lin
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2017, 700 : 681 - 689
  • [48] Kinetics of nanoscale precipitation in Ni-Fe-Al alloys: A magnetic monitoring approach
    Duman, Nagehan
    Mekhrabov, Amdulla O.
    Akdeniz, M. Vedat
    JOURNAL OF ALLOYS AND COMPOUNDS, 2011, 509 (24) : 6781 - 6786
  • [49] Microstructure and mechanical behavior of directionally solidified Fe35Ni15Mn25Al25
    Wu, X.
    Baker, I.
    Miller, M. K.
    More, K. L.
    Bei, H.
    Wu, H.
    INTERMETALLICS, 2013, 32 : 413 - 422
  • [50] DUCTILITY AT HIGH-TEMPERATURE AND CREEP-BEHAVIOR OF DIRECTIONALLY SOLIDIFIED NI-CR-BASE ALLOYS
    MORGAN, WR
    GIBBONS, TB
    METALS TECHNOLOGY, 1980, 7 (MAY): : 197 - 202