Strong covalent bonding modulated graphene oxide/epoxy interfacial enhancement and advanced corrosion resistance

Chemically functionalized graphene oxide [multi-amino functionalized graphene oxide (MAGO)] was achieved by building covalent bonds between graphene oxide (GO) and a small molecule containing benzene structure and multi-amino groups. Fourier transform infrared, X-ray diffraction, X-ray photo electron spectroscopy and TEM-EDX results certified that the molecule was successfully grafted onto GO nanosheets. Subsequently, functionalized GO was incorporated into waterborne epoxy (EP) coating through ball-milling method. This molecular design can significantly improve the dispersion of MAGO in EP matrix, as well as the compatibility and interaction between MAGO and EP. Compared with GO/EP, the water absorption of MAGO/EP decreased from 4.38 to 2.59%, the adhesion strength of MAGO/EP increased from 4.72 to 6.32 MPa after immersion of 40 days in 3.5% NaCl solution. Incorporation of 1 wt% of MAGO into EP matrix prominently improved the long-term corrosion resistance. The impedance modulus of GO/EP coating decreased by four orders after 40 days immersion, while that of MAGO/EP coating only decreased by one order. The impedance modulus was still 1.47 x 10(8) omega cm(2), and two-time constant wasn't detected for MAGO/EP coating. This research developed a novel green anticorrosion coating with enhanced durability for metal protection.