Pulse electric current sintering of iron-base powders prepared by high energy milling

被引：2
|
作者：
Li, Y. Y. [1 ]
Li, X. Q. [1 ]
Long, Y. [1 ]
Shao, M. [1 ]
Xia, W. [1 ]
机构：
[1] S China Univ Technol, Coll Mech Engn, Guangzhou 510640, Peoples R China
来源：
ADVANCES IN MACHINING & MANUFACTURING TECHNOLOGY VIII | 2006年 / 315-316卷
关键词：
iron base powder; high energy milling; pulse electric current sintering; density; microstructure and performance;
D O I：
10.4028/www.scientific.net/KEM.315-316.445
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Fe-2Cu-2Ni-1Mo-0.8C (wt. pct) alloys were successfully fabricated from elemental mixed powders by high energy milling and pulse electric current sintering, and the effects of milling time and sintering parameters on the densification degree, microstructure, mechanical properties and fracture characteristic of sintered material were investigated. Results showed that with increasing milling time, pulse electric current peak and sintering time, the density and transverse rupture strength of sintered alloy were improved. However, higher pulse electric current peak and/or longer sintering time were unfavorable to the density and strength of sintered alloy, because of generating overhigh sintering temperature. The density and transverse rupture strength of sintered alloy could reach 7.74 X 10(3) kg/m(3) and 2231 MPa, respectively, and the corresponding fracture morphology was characterized as intergranular fracture.
引用
收藏
页码：445 / 449
页数：5
相关论文
共 50 条
  • [41] Equivalent resistance in pulse electric current sintering
    Zhang, DM
    Fu, ZY
    Yuan, RZ
    Guo, JK
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2002, 17 (02): : 30 - 32
  • [42] Equivalent resistance in pulse electric current sintering
    Dong-ming Z.
    Zheng-yi F.
    Run-zhang Y.
    Jing-kun G.
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2002, 17 (2): : 30 - 32
  • [43] Hydroxyapatite/iron oxide nanocomposite prepared by high energy ball milling
    Vasic, Milica Vucinic
    Antic, Bratislav
    Boskovic, Marko
    Antic, Aleksandar
    Blanusa, Jovan
    PROCESSING AND APPLICATION OF CERAMICS, 2019, 13 (02) : 210 - 217
  • [44] Device for electric-pulse sintering of powders under pressure
    I. M. Mal’tsev
    V. A. Baranov
    Powder Metallurgy and Metal Ceramics, 2000, 39 : 109 - 112
  • [45] Device for electric-pulse sintering of powders under pressure
    Mal'tsev, IM
    Baranov, VA
    POWDER METALLURGY AND METAL CERAMICS, 2000, 39 (1-2) : 109 - 112
  • [46] High energy milling on tungsten powders
    Kiran, U. Ravi
    Kumar, M. Prem
    Sankaranarayana, M.
    Singh, A. K.
    Nandy, T. K.
    INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2015, 48 : 74 - 81
  • [47] Stacking fault energy of iron-base shape memory alloys
    Li, JC
    Zheng, W
    Jiang, Q
    MATERIALS LETTERS, 1999, 38 (04) : 275 - 277
  • [48] Microwave properties of powders produced by high-energy milling of iron with paraffin
    Rozanov, K. N.
    Petrov, D. A.
    Maratkanova, A. N.
    Chulkina, A. A.
    Lomayeva, S. F.
    PHYSICS OF METALS AND METALLOGRAPHY, 2014, 115 (07): : 642 - 649
  • [49] Microwave properties of powders produced by high-energy milling of iron with paraffin
    K. N. Rozanov
    D. A. Petrov
    A. N. Maratkanova
    A. A. Chulkina
    S. F. Lomayeva
    The Physics of Metals and Metallography, 2014, 115 : 642 - 649
  • [50] Characterization of thermoelectric metal oxide elements prepared by the pulse electric-current sintering method
    Fujishiro, Y
    Miyata, M
    Awano, M
    Maeda, K
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2004, 87 (10) : 1890 - 1894
12345