Influence of Silica Filler Addition on Fatigue Crack Propagation Rate of Underfill Resin

被引：2

作者：

Ishibashi, Jun ^{[1
]}

Kariya, Yoshiharu ^{[2
]}

Satoh, Toshiyuki ^{[3
]}

Enomoto, Toshiaki ^{[3
]}

Yamaguchi, Hiroshi ^{[3
]}

机构：

[1] Shibaura Inst Technol, Grad Sch, Tokyo 1358548, Japan

[2] Shibaura Inst Technol, Dept Mat Sci & Engn, Tokyo 1358548, Japan

[3] NAMICS Corp, Niigata 9503102, Japan

来源：

MATERIALS TRANSACTIONS | 2019年 / 60卷 / 06期

关键词：

fatigue; fatigue crack propagation; underfill resin; epoxy; silica filler; FEM analysis; FRACTURE-TOUGHNESS; EPOXY; BEHAVIOR;

D O I：

10.2320/matertrans.MH201812

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In this study, fatigue crack propagation testing on underfill resins with different filler content and finite element method (FEM) analysis were carried out to investigate the effects of filler content on fatigue crack propagation rate. The fatigue crack propagation rate of the underfill resin decreased with increasing filler content. FEM analysis clearly showed that fillers constrain the deformation of resin around them, which leads to inhibition of the amount of crack opening and a decrease in the energy release rate surrounding a crack tip. Since the amount of crack opening decreased with increasing filler content, it is conceivable that the decreased fatigue crack propagation rate can be attributed to a decrease in the amount of crack opening. The constraint on deformation of the base resin implies an increase in macroscopic static strength, and thus the resistance to fatigue crack propagation correlates with static strength.

引用

页码：902 / 908

页数：7

共 50 条

[41] SURFACE FATIGUE CRACK-PROPAGATION BEHAVIOR IN A RESIDUAL-STRESS FIELD - FATIGUE CRACK-GROWTH LAW AND EVALUATION OF FATIGUE CRACK-PROPAGATION RATE
TORII, T
HONDA, K
SUGIYAMA, M
JSME INTERNATIONAL JOURNAL SERIES I-SOLID MECHANICS STRENGTH OF MATERIALS, 1989, 32 (03): : 450 - 457
[42] The influence of the base material - filler metal pairing on the fatigue crack propagation of 700 MPa strength category welded joints
Lukacs, J.
Mobark, H. F. H.
12TH HUNGARIAN CONFERENCE ON MATERIALS SCIENCE (HMSC12), 2020, 903
[43] ANALYSIS OF FATIGUE CRACK PROPAGATION RATE BY SCANNING ELECTRON MICROSCOPY
WOLFF, UE
JOURNAL OF ULTRASTRUCTURE RESEARCH, 1970, 30 (1-2): : 242 - &
[44] FATIGUE FRACTURE-TOUGHNESS AND CRACK-PROPAGATION RATE
SAWAKI, Y
TADA, S
HASHIMOTO, S
KAWASAKI, T
INTERNATIONAL JOURNAL OF FRACTURE, 1987, 35 (02) : 125 - 137
[45] RELATION BETWEEN SEPARATION OF CRACKS AND PROPAGATION RATE OF FATIGUE CRACK
BATHIAS, C
DEFOUQUE.J
DELEIRIS, H
COMPTES RENDUS HEBDOMADAIRES DES SEANCES DE L ACADEMIE DES SCIENCES SERIE A, 1972, 274 (10): : 867 - &
[46] EFFECT OF TEMPERATURE ON FATIGUE CRACK-PROPAGATION RATE IN ALUMINUM
LIAW, PK
FINE, ME
KIRITANI, M
ONO, S
SCRIPTA METALLURGICA, 1977, 11 (12): : 1151 - 1155
[47] Analysis of the effects of compressive stresses on fatigue crack propagation rate
Zhang, J.
He, X. D.
Du, S. Y.
INTERNATIONAL JOURNAL OF FATIGUE, 2007, 29 (9-11) : 1751 - 1756
[48] MECHANICAL LOADING AND CYCLIC HEATING PHASE SHIFT EFFECT ON FATIGUE CRACK PROPAGATION RATE. PART 2. FATIGUE CRACK PROPAGATION RATE PREDICTION
Gopkalo, A. P.
Novikov, A. I.
STRENGTH OF MATERIALS, 2011, 43 (04) : 384 - 395
[49] Mechanical loading and cyclic heating phase shift effect on fatigue crack propagation rate. Part 2. Fatigue crack propagation rate prediction
A. P. Gopkalo
A. I. Novikov
Strength of Materials, 2011, 43 : 384 - 395
[50] INFLUENCE OF MEAN STRESS ON CRACK CLOSURE PHENOMENON AND FATIGUE CRACK-PROPAGATION
NISITANI, H
TAKAO, K
BULLETIN OF THE JSME-JAPAN SOCIETY OF MECHANICAL ENGINEERS, 1977, 20 (141): : 264 - 270

← 1 2 3 4 5 →