Study on rolling of a new near-α titanium alloy: Microstructure refinement and dual-scale silicides evolution

被引:20
|
作者
Su, Yu [1 ,2 ]
Hao, Guojian [3 ]
Fan, Haoyu [4 ]
Zhai, Yuewen [3 ]
Kong, Fantao [1 ,2 ]
Wang, Xiaopeng [2 ]
Chen, Yuyong [1 ,2 ]
机构
[1] Harbin Inst Technol, State Key Lab Adv Welding & Joining, Harbin 150001, Peoples R China
[2] Harbin Inst Technol, Sch Mat Sci & Engn, POB 434, Harbin 150001, Peoples R China
[3] Beijing Res Inst Mech & Elect Technol, Beijing 100083, Peoples R China
[4] Beijing Huahang Radio Measurement Inst, Beijing 100013, Peoples R China
基金
中国国家自然科学基金;
关键词
Near-alpha titanium alloy sheet; Rolling reductions; Microstructure refinement; Dual-scale silicides; Tensile properties; Strengthening mechanisms; METAL-MATRIX NANOCOMPOSITES; MECHANICAL-PROPERTIES; TENSILE PROPERTIES; HOT-WORKING; AS-CAST; DEFORMATION; TEMPERATURE; BEHAVIOR; PRECIPITATION; PREDICTION;
D O I
10.1016/j.jallcom.2020.156867
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
In this study, a novel near-a titanium alloy sheet with dual-scale silicides was successfully fabricated by rolling in alpha+beta two phase field. The microstructure refinement, dual-scale silicides evolution and their influence on the tensile properties were systematically investigated. The results indicate that the preheating before rolling and the reheating between rolling passes play vital roles in the process of microstructure refinement. Thus, a new microstructure refinement mechanism was proposed considering the heat treatment besides the rolling deformation. The dual-scale silicides exhibit obvious differences in size, shape and distribution. The mean size of large-scale silicides is about 1.58 mu m while the one of small-scale silicides is only 152 nm. The sheet with dual-scale silicides shows an outstanding room temperature tensile strength (1370 MPa) but an ordinary 650 degrees C tensile strength (513 MPa). This is because the strengthening mechanisms can be attributed to the microstructure refinement, dual-scale silicides and the residual substructures at room temperature. At 650 degrees C, however, the matrix softening is dominant due to the directionally arranged alpha/beta microstructure has a low flow resistance at high temperature. (C) 2020 Elsevier B.V. All rights reserved.
引用
收藏
页数:11
相关论文
共 50 条
  • [21] Microstructure evolution and mechanical properties of a lamellar near-α titanium alloy treated by laser shock peening
    Jia, Weiju
    Zan, Yaoxu
    Mao, Chengliang
    Li, Silan
    Zhou, Wei
    Li, Qian
    Zhang, Siyuan
    Ji, Vincent
    VACUUM, 2021, 184
  • [22] Phase Transformation and Microstructure Evolution in Near-β Ti-7333 Titanium Alloy During Aging
    Hui, Qiong
    Xue, Xiangyi
    Kou, Hongchao
    Lai, Minjie
    Tang, Bin
    Li, Jinshan
    HIGH PERFORMANCE STRUCTURE MATERIALS, 2013, 747-748 : 904 - 911
  • [23] Effect of α′ Martensite on Microstructure Refinement After α plus β Isothermal Treatment in a Near-α Titanium Alloy Ti60
    Sun, Feng
    Li, Jinshan
    Kou, Hongchao
    Tang, Bin
    Cai, Jianming
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2015, 24 (05) : 1945 - 1952
  • [24] Microstructure evolution of near-α titanium alloys during thermomechanical processing
    Ma, FC
    Lu, WJ
    Qin, JN
    Zhang, D
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 416 (1-2): : 59 - 65
  • [25] Hot deformation mechanism and microstructure evolution of a new near β titanium alloy
    Fan, J. K.
    Kou, H. C.
    Lai, M. J.
    Tang, B.
    Chang, H.
    Li, J. S.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2013, 584 : 121 - 132
  • [26] Precipitation of ordered α2 phase in a near-α titanium alloy with duplex microstructure
    Jun Zhang and Dong Li1) Shenyang University
    Journal of University of Science and Technology Beijing(English Edition), 2002, (03) : 202 - 205
  • [27] Precipitation of ordered α2 phase in a near-α titanium alloy with duplex microstructure
    Zhang, Jun
    Li, Dong
    Journal of University of Science and Technology Beijing: Mineral Metallurgy Materials (Eng Ed), 2002, 9 (03): : 202 - 205
  • [28] Precipitation of ordered α2 phase in a near-α titanium alloy with duplex microstructure
    Zhang, J
    Li, D
    JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING, 2002, 9 (03): : 202 - 205
  • [29] Microstructure evolution characteristics of near-α TA32 titanium alloy during superplastic tensile deformation
    Liu, Yang
    Li, Zhiqiang
    Zhao, Bing
    Sun, Chaoyang
    Feng, Yinghao
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2023, 879
  • [30] Microstructure development and properties of the AlCuFe quasicrystalline coating on near-α titanium alloy
    Moskalewicz, T.
    Kot, M.
    Wendler, B.
    APPLIED SURFACE SCIENCE, 2011, 258 (02) : 848 - 859