Ultra-high cycle fatigue behavior of high strength steel with carbide-free bainite/martensite complex microstructure

被引：14
|
作者：
Xu, Xue-xia [1 ]
Yu, Yang [1 ]
Cui, Wen-long [1 ]
Bai, Bing-zhe [1 ]
Gu, Jia-lin [1 ]
机构：
[1] Tsinghua Univ, Dept Mat Sci & Engn, Adv Mat Lab, Beijing 100084, Peoples R China
来源：
INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS | 2009年 / 16卷 / 03期
关键词：
high strength steel; ultra-high cycle fatigue; bainite; martensite; fatigue behavior; CRACK INITIATION; MECHANISM; FAILURE; LIMIT; LIFE;
D O I：
10.1016/S1674-4799(09)60051-0
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The ultra-high cycle fatigue behavior of a novel high strength steel with carbide-free bainite/martensite (CFB/M) complex microstructure was studied. The ultra-high cycle fatigue properties were measured by ultrasonic fatigue testing equipment at a frequency of 20 kHz. It is found that there is no horizontal part in the S-N curve and fatigue fracture occurs when the life of specimens exceeds 10(7) Cycles. In addition, the origination of fatigue cracks tends to transfer from the surface to interior of specimens as the fatigue cycle exceeds 10(7), and the fatigue crack originations of many specimens are not induced by inclusions, but by some kind of "soft structure". It is shown that the studied high strength steel performs good ultra-high cycle fatigue properties. The ultra-high fatigue mechanism was discussed and it is suggested that specific CFB/M complex microstructure of the studied steel contributes to its superior properties.
引用
收藏
页码：285 / 292
页数：8
相关论文
共 50 条
  • [31] Variant Pairing of Lath Bainite and Martensite in an Ultra-High-Strength Steel
    Li, Meiying
    Wang, Shun
    Jia, Tao
    Zhao, Xianming
    METALS, 2022, 12 (11)
  • [32] Effects of Plastic Stress on Transformation Plasticity and Microstructure of a Carbide-Free Bainite Steel
    Liu, Mengen
    Ma, Ying
    Xu, Guang
    Cai, Guangyu
    Zhou, Mingxing
    Zhang, Xi
    METALLOGRAPHY MICROSTRUCTURE AND ANALYSIS, 2019, 8 (02) : 159 - 166
  • [33] Effects of Plastic Stress on Transformation Plasticity and Microstructure of a Carbide-Free Bainite Steel
    Mengen Liu
    Ying Ma
    Guang Xu
    Guangyu Cai
    Mingxing Zhou
    Xi Zhang
    Metallography, Microstructure, and Analysis, 2019, 8 : 159 - 166
  • [34] Fatigue behavior on a 1500 MPa grade bainite/martensite duplex-phase high strength steel
    Wei, DY
    Gu, JL
    Fang, HS
    Bai, BZ
    ACTA METALLURGICA SINICA, 2003, 39 (07) : 734 - 738
  • [35] Relationship between non-inclusion induced crack initiation and microstructure on fatigue behavior of bainite/martensite steel in high cycle fatigue/very high cycle (HCF/VHCF) regime
    Gui, Xiaolu
    Gao, Guhui
    An, Baifeng
    Misra, R.D.K.
    Bai, Bingzhe
    Materials Science and Engineering: A, 2021, 803
  • [36] Relationship between non-inclusion induced crack initiation and microstructure on fatigue behavior of bainite/martensite steel in high cycle fatigue/very high cycle (HCF/VHCF) regime
    Gui, Xiaolu
    Gao, Guhui
    An, Baifeng
    Misra, R. D. K.
    Bai, Bingzhe
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2021, 803
  • [37] Low cycle fatigue behavior in a medium-carbon carbide-free bainitic steel
    Kang, J.
    Zhang, F. C.
    Long, X. Y.
    Lv, B.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 666 : 88 - 93
  • [38] Cyclic deformation behaviors of a high strength carbide-free bainitic steel
    Zhang, F. C.
    Long, X. Y.
    Kang, J.
    Cao, D.
    Lv, B.
    MATERIALS & DESIGN, 2016, 94 : 1 - 8
  • [39] Fatigue crack growth behaviour of a Si–Mn steel with carbide-free lathy bainite
    LIU WENYAN
    QU JINGXIN
    SHAO HESHENG
    Journal of Materials Science, 1997, 32 (2) : 427 - 430
  • [40] Notch fatigue behavior: Metallic glass versus ultra-high strength steel
    X. D. Wang
    R. T. Qu
    S. J. Wu
    Q. Q. Duan
    Z. Q. Liu
    Z. W. Zhu
    H. F. Zhang
    Z. F. Zhang
    Scientific Reports, 6
12345