STUDY OF BENZOTRIAZOLE AS CORROSION INHIBITORS OF CARBON STEEL IN CHLORIDE SOLUTION CONTAINING HYDROGEN SULFIDE USING ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY (EIS)

Corrosion and inhibition studies on API 5LX65 carbon steel M chloride solution containing various concentrations of benzotriazole has been conducted at temperature of 70 degrees C using Electrochemical Impedance Spectroscopy (EIS). Corroded carbon steel surface with and without inhibitor have been observed using X-ray Diffraction (XRD), Scanning Electron Microscope (SEM), and Energy Dispersive Spectroscopy (EDS). The objectives of this research are to study the performance of benzotriazole as corrosion inhibitors. The experimental results of carbon steel corrosion in 3.5% NaCl solution containing 500 mg/l H2S at different BTAH concentrations showed that corrosion rate of carbon steel decreases with increasing of BTAH concentrations from 0 to 10 mmol/l. The inhibition efficiency of BTAH was found to be affected by its concentration. The optimum efficiency obtained of BTAH is 93% at concentration of 5 mmol/l. The result of XRD and EDS analysis reveal the iron sulfide (FeS) formation on corroded carbon steel surface without inhibitor. The EDS spectrum show the Nitrogen (N) bond on carbon steel surface inhibited by BTAH.