Study of air heat treatment on Bi-2223/Ag superconducting tapes

被引：3
|
作者：
Guo Wei [1 ,2 ,3 ]
Zou Guisheng [1 ,2 ]
Wu Aiping [1 ,2 ]
Wang Yanjun [1 ,2 ]
Bai Hailin [1 ,2 ]
Ren Jialie [1 ,2 ]
机构：
[1] Tsinghua Univ, Dept Mech Engn, Beijing 100084, Peoples R China
[2] Minist Educ PR China, Key Lab Adv Mfg Mat Proc Technol, Beijing 100084, Peoples R China
[3] Beijing Univ Aeronaut & Astronaut, Sch Mech Engn & Automat, Beijing 100191, Peoples R China
来源：
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS | 2009年 / 469卷 / 13期
基金：
中国国家自然科学基金; 中国博士后科学基金; 北京市自然科学基金;
关键词：
Bi-2223/Ag tape; Heat treatment; Critical current; EVOLUTION; TEMPERATURE; TIME;
D O I：
10.1016/j.physc.2009.04.010
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
Heat treatment has been carried out on commercially available Bi-2223/Ag superconducting tape under various temperature conditions in air. The critical currents (I-c) of tape after heat treatment at different annealing temperatures were tested at the liquid-nitrogen temperature. The microstructures and phase constituents of the tapes were investigated by SEM and XRD, respectively. The results indicate that annealing temperature has a very important influence on the superconducting properties of the tapes. When the temperature is above 840 degrees C, I-c value drops dramatically. Furthermore, when the temperature reaches up to 860 degrees C, the tape loses most of its superconducting property because of the decomposition of the superconducting phase Bi-2223. (c) 2009 Elsevier B.V. All rights reserved.
引用
收藏
页码：778 / 781
页数：4
相关论文
共 50 条
  • [31] AC loss from susceptibility measurements in Bi-2223/Ag superconducting tapes
    Muller, KH
    Savvides, N
    Katsaros, A
    Guo, YC
    Dou, SX
    CZECHOSLOVAK JOURNAL OF PHYSICS, 1996, 46 : 1297 - 1298
  • [32] Effect of the different precursor powder on the superconducting property of Bi-2223/Ag tapes
    Yu, ZM
    Li, CS
    Xiong, XM
    Zhang, HL
    Zhang, PX
    Zhou, L
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2002, 378 (PART 2): : 1083 - 1086
  • [33] Cold pressing and its effect on microstructure of (Bi-2223)/Ag superconducting tapes
    Ma, Yanwei
    Wang, Zutang
    Fenmo Yejin Jishu/Powder Metallurgy Technology, 1998, 16 (01): : 21 - 25
  • [34] LONG MULTIFILAMENT BI-2223 AG-SHEATHED SUPERCONDUCTING TAPES AND SOLENOIDS
    YAU, J
    LIU, HK
    DOU, SX
    KATSAROS, A
    SAVVIDES, N
    JOURNAL OF SUPERCONDUCTIVITY, 1994, 7 (05): : 829 - 833
  • [35] Investigation on the phase transformation of Bi-2223/Ag superconducting tapes during heating
    Huang, K. -T.
    Qu, T. -M.
    Xie, P.
    Han, Z.
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2013, 490 : 43 - 48
  • [36] Effect of strain on ac power loss of Bi-2223/Ag superconducting tapes
    CSIRO Telecommunications and, Industrial Physics, Sydney
    Phys C Supercond, 1-2 (129-135):
  • [37] Shape of magnetic hysteresis loop measured on superconducting Bi-2223/Ag tapes
    Pust, L
    Galkin, A
    Koblischka, MR
    CZECHOSLOVAK JOURNAL OF PHYSICS, 1996, 46 : 1603 - 1604
  • [38] AC losses in superconducting Ag/Bi-2223 composite tapes with interfilamentary barrier
    Ciszek, M
    Tsukamoto, O
    Ogawa, J
    Amemiya, N
    Hayashi, K
    Ueyama, M
    Ayai, N
    PHYSICA C, 2001, 357 (SUPPL. 1): : 1226 - 1229
  • [39] Improved uniformity of microstructure and electrical properties of Bi-2223/Ag superconducting tapes
    Guo, YC
    Chen, WM
    Liu, HK
    Dou, SX
    Lukashenko, AV
    PHYSICA C, 2001, 355 (1-2): : 163 - 171
  • [40] Fabrication of joint Bi-2223/Ag superconducting tapes with BSCCO superconducting powders by diffusion bonding
    Wei Guo
    Zou Guisheng
    Wu Aiping
    Zhou Fangbing
    Ren Jialie
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2010, 470 (9-10): : 440 - 443
12345