Mechanical & Morphological Properties of Attapulgite/NR Composites: Effect of Mixing Time Variation

The development of composite material based on attapulgite clay (ATP) as a filler and natural rubber (NR) matrices were prepared by combination of melt mixing and latex compounding methods. Sonication technique was chosen in this work to disperse the attapulgite suspension. 6 phr of attapulgite loading was fabricated using different time of mixing ranging from 30 minutes until 2 hours and sonication time was kept constant at 15 minutes. Then, co-coagulating HA latex with attapulgite clay suspension through latex compounding method produced the masterbatch. The masterbatch was compounded with natural rubber by melt mixing method. The mechanical and morphological characteristics were investigated in this work. From mechanical testing, M1 showed the highest value of tensile and tear strength. By comparing with M30 and M2, M1 shows high 300% tensile modulus and lower crosslink density. However, when the time of mixing was prolonged to 2 hours, the results for tensile strength, elongation at break and tear strength were decreased. This is due to flocculation of attapulgite particles. Sonication techniques also proved that the tensile strength and elongation at break of these three samples were higher compared to gum NR (NR) and attapulgite compounded with NR using a conventional method (in-situ 6). From field emission scanning electron microscope (FESEM) results, it revealed that M1 had good dispersion in the NR system. It is proved that the higher tensile strength was due to good dispersion of attapulgite clay in the NR matrix. It was also supported from crosslink density, which is lower than NR and in-situ 6 results. It showed that the penetration of toluene solvent into rubber compound was restricted. The optimum time, M1 give the best results, which can be compared to control the sample.