Strengthen Air Oxidation of Refractory Humic Acid Using Reductively Etched Nickel-Cobalt Spinel Catalyst

Nickel-cobalt spinel catalyst (NCO) is a promising catalyst for air oxidation of humic acid, which is a typical natural refractory organic matter and a precursor of toxic disinfection by-products. In this study, reductive etchers, NaBH4 or Na2SO3, were used to adjust the NCO surface structure to increase the performance. The modified catalyst (NCO-R) was characterized, and the relationship between its intrinsic properties and catalytic paths was discovered. The results of O-2-temperature programmed desorption, NH3-temperature programmed desorption, and X-ray photoelectron spectroscopy (XPS) demonstrated that reductant etching introduced oxygen vacancies to the surface of NCO and increased active surface oxygen species and surface acidity. In addition, the modification did not change the raw hollow sphere structure of NCO. The crystallinity and specific surface area of NCO-R increased, and average pore size of NCO-R decreased. XPS results showed that the ratio of Co3+/Co2+ in NCO-R decreased compared with NCO, while the ratio of Ni3+/Ni2+ increased. The results of H-2-temperature programmed reduction showed that the H-2 reduction ability of NCO-R was stronger. Due to these changes in chemical and physical properties, NCO-R exhibited much better catalytic performance than NCO. In the catalytic air oxidation of humic acid at 25 degrees C, the total organic carbon (TOC) removal rate increased significantly from 44.4% using NCO to 77.0% using NCO-R. TOC concentration of humic acid decreased by 90.0% after 12 h in the catalytic air oxidation using NCO-R at 90 degrees C.