Investigations on high SO3 portland clinkers and cements .1. Clinker synthesis and cement preparation

被引：37
|
作者：
Odler, I
Zhang, H
机构：
[1] Technical University Clausthal, Clausthal-Zellerfeld
来源：
CEMENT AND CONCRETE RESEARCH | 1996年 / 26卷 / 09期
关键词：
D O I：
10.1016/0008-8846(96)00128-7
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
Portland clinkers containing side by side the phases C3S, and C(4)A(3s) and optionally also C(4)AF and C2S, ay be produced by burning pertinent raw meals with added small amounts of CaF2 to temperatures 1250-1300 degrees C. Such clinkers exhibit a significantly improved grindability as compared to ordinary portland cement clinker. The Sterength development of cements made from these clinkers depends greatly on the amount of added gypsum and at optimum gypsum additions is similar to that of ordinary portland cement.
引用
收藏
页码：1307 / 1313
页数：7
相关论文
共 50 条
  • [41] Influence of the Content of Alkalis (Na2O and K2O), MgO, and SO3 Present in the Granite Rock Fine in the Production of Portland Clinker
    Santos, Tiago A.
    Andrade Neto, Jose S.
    Cilla, Marcelo S.
    Ribeiro, Daniel, V
    JOURNAL OF MATERIALS IN CIVIL ENGINEERING, 2022, 34 (03)
  • [42] INVESTIGATIONS ON THE RELATIONSHIP BETWEEN POROSITY, STRUCTURE AND STRENGTH OF HYDRATED PORTLAND-CEMENT PASTES .1. EFFECT OF POROSITY
    ROSSLER, M
    ODLER, I
    CEMENT AND CONCRETE RESEARCH, 1985, 15 (02) : 320 - 330
  • [43] Research on the formation of M1-type alite doped with MgO and SO3-A route to improve the quality of cement clinker with a high content of MgO
    Zhou, Hao
    Gu, Xiaomei
    Sun, Jinfeng
    Yu, Zhuqing
    Huang, Hong
    Wang, Qianqian
    Shen, Xiaodong
    CONSTRUCTION AND BUILDING MATERIALS, 2018, 182 : 156 - 166
  • [44] Influence of SO3 amount in high volume blast furnace slag cement on fire-induced explosive spalling resistance
    Tsuji D.
    Kojima M.
    Ohtsuka Y.
    Noguchi T.
    Journal of Structural and Construction Engineering, 2019, 84 (756): : 119 - 127
  • [45] INVESTIGATIONS ON THE STRUCTURE OF FULLY HYDRATED PORTLAND-CEMENT AND TRICALCIUM SILICATE PASTES .1. BOUND WATER, CHEMICAL SHRINKAGE AND DENSITY OF HYDRATES
    KOSTER, H
    ODLER, I
    CEMENT AND CONCRETE RESEARCH, 1986, 16 (02) : 207 - 214
  • [46] GLASS IONOMER CEMENT FORMULATIONS .1. PREPARATION OF NOVEL FLUOROALUMINOSILICATE GLASSES HIGH IN FLUORINE
    KENT, BE
    LEWIS, BG
    WILSON, AD
    JOURNAL OF DENTAL RESEARCH, 1979, 58 (06) : 1607 - 1619
  • [47] Synthesis and characterization of bacterial cellulose sulfates using a SO3/pyridine complex in DMAc/LiC1
    Qin, Ziyu
    Ji, Li
    Yin, Xueqiong
    Zhu, Li
    Lin, Qiang
    Qin, Jinming
    CARBOHYDRATE POLYMERS, 2014, 101 : 947 - 953
  • [48] A 4-1 RANGE IN CONCRETE CREEP WHEN CEMENT SO3 CONTENT, CURING TEMPERATURE AND FLY-ASH CONTENT ARE VARIED
    ALEXANDER, KM
    WARDLAW, J
    IVANUSEC, I
    CEMENT AND CONCRETE RESEARCH, 1986, 16 (02) : 173 - 180
  • [49] OXIDATION OF CARBON-MONOXIDE ON A PALLADIZED VANADIUM POTASSIUM-SULFATE CATALYST IN THE PRESENCE OF SO2, SO3, AND H2O .1.
    MARTSENYUKKUKHARUK, MG
    ORLIK, SN
    VYSOCHENKO, VG
    KORNEICHUK, GP
    KINETICS AND CATALYSIS, 1983, 24 (02) : 307 - 310
  • [50] MANUFACTURE OF MODIFIED PORTLAND CEMENTS WITH FLY-ASH AND BLAST-FURNACE SLAG IN THE NORWEGIAN CEMENT INDUSTRY .1. RESEARCH-DEVELOPMENT QUALITY CONSIDERATIONS SYSTEM-PLANNING
    HANSSON, ES
    SOEPLER, B
    ZEMENT-KALK-GIPS, 1982, 35 (12): : 625 - 633
12345