Numerical Simulation of Zr-based Bulk Metallic Glass During Continuous Casting Solidification Process

被引：4
|
作者：
Tang, Renhong [1 ]
Zhou, Bingwen [1 ]
Ma, Yuejiao [1 ]
Jia, Fei [1 ]
Zhang, Xingguo [1 ]
机构：
[1] Dalian Univ Technol, Sch Mat Sci & Engn, Dalian 116024, Peoples R China
来源：
MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS | 2015年 / 18卷
基金：
中国国家自然科学基金;
关键词：
bulk metallic glass; continuous casting; composite water cold copper-graphite mold; numerical simulation of casting process; temperature field; THERMAL-STABILITY; FORMING ABILITY; 30; MM; DIAMETER; ALLOYS; COMPOSITE; MOLD;
D O I：
10.1590/1516-1439.319814
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
A numerical simulation method was used to analyze the solidification process of Zr-based bulk metallic glass (BMG) during the horizontal continuous casting (HCC) process. The large-scale general-purpose finite element analysis software ANSYS was adopted to develop a temperature field model. The variation of temperature field in the specific area at different time was studied. Its accuracy was verified by the experimental results of Zr48Cu36Ag8Al8 bulk metallic glass continuous casting solidification process. The effects of casting parameters include intermittent casting procedure (drawing and stopping), casting speed, pouring temperature and cooling rate. The results show that the optimum casting speed range is 1-2 mm/s, pouring temperature is 1223 K and cooling rate of 10 mm rod casting is 5 L/min respectively. A fully Zr-based bulk metallic glass whose diameter is 10 mm and length has no limitation has been successfully fabricated.
引用
收藏
页码：3 / 9
页数：7
相关论文
共 50 条
  • [41] Indentation creep behavior of a Zr-based bulk metallic glass
    Department of General Physics, Eötvös University, P.O.B. 32, Budapest, H-1518, Hungary
    不详
    Journal of Alloys and Compounds, 2007, 434-435 (SPEC. ISS.): : 75 - 78
  • [42] The fatigue endurance limit of a Zr-based bulk metallic glass
    Menzel, Brian C.
    Dauskardt, Reinhold H.
    SCRIPTA MATERIALIA, 2006, 55 (07) : 601 - 604
  • [43] Dynamic mechanical behavior of a Zr-based bulk metallic glass during glass transition and crystallization
    Chao Qi
    Wang Qing
    Dong Yuanda
    RARE METALS, 2009, 28 (01) : 72 - 76
  • [44] Stable fracture of a malleable Zr-based bulk metallic glass
    Sun, B. A.
    Tan, J.
    Pauly, S.
    Kuehn, U.
    Eckert, J.
    JOURNAL OF APPLIED PHYSICS, 2012, 112 (10)
  • [45] Indentation creep behavior of a Zr-based bulk metallic glass
    Fatay, D.
    Gubicza, J.
    Lendvai, J.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2007, 434 : 75 - 78
  • [46] Temperature Effect on Fracture of a Zr-Based Bulk Metallic Glass
    Yang, Na
    Yi, Jun
    Yang, Yu Hang
    Huang, Bo
    Jia, Yan Dong
    Kou, Sheng Zhong
    Wang, Gang
    MATERIALS, 2020, 13 (10)
  • [47] Compressive fracture characteristics of Zr-based bulk metallic glass
    FAN ZhenJun
    Science China(Physics,Mechanics & Astronomy), 2010, (05) : 823 - 827
  • [48] Reciprocating wear mechanisms in a Zr-based bulk metallic glass
    Jin H.W.
    Ayer R.
    Koo J.Y.
    Raghavan R.
    Ramamurty U.
    Journal of Materials Research, 2007, 22 (2) : 264 - 273
  • [49] Ambient temperature embrittlement of a Zr-based bulk metallic glass
    Jiang, F.
    Wang, H. F.
    Jiang, M. Q.
    Li, G.
    Zhao, Y. L.
    He, L.
    Sun, J.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 549 : 14 - 19
  • [50] Microstructural studies of crystallization of a Zr-based bulk metallic glass
    Pekarskaya, E
    Löffler, JF
    Johnson, WL
    ACTA MATERIALIA, 2003, 51 (14) : 4045 - 4057
12345