Preparation and Properties of RDX/Aluminum Composites by Spray-Drying Method

RDX/aluminum composites were prepared by the spray-drying method with F-2602 as a binder. The morphology and covering effect of composites were characterized by scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). The effect of the processing parameters on the morphology of the samples was investigated. The impact sensitivity and thermal decomposition behavior of RDX/aluminum composites were also measured and analyzed. Optimal morphology of samples was achieved when the inlet temperature, nitrogen flow rate, and suspension feed flow rates were 80 degrees C, 473 L center dot h(-1), and 4.5 mL center dot min(-1), respectively. In addition, RDX/aluminum composites with the same content were prepared by a coverage-mixing method for comparative analysis. Experimental results showed that the thermal sensitivity and the impact sensitivity of RDX/aluminum composites prepared by the spray-drying method were significantly lower than those of RDX/aluminum composites prepared by the coverage-mixing method.