Surface science studies of the effect of Mn2+ on zinc phosphating of 2024-T3 Al alloy

被引：4
|
作者：
Akhtar, A. S. [1 ]
Susac, D. [1 ]
Wong, K. C. [1 ]
Wong, P. C. [1 ]
Mitchell, K. A. R. [1 ]
机构：
[1] Univ British Columbia, Dept Chem, Vancouver, BC V5Z 1M9, Canada
来源：
ALUMINIUM ALLOYS 2006, PTS 1 AND 2: RESEARCH THROUGH INNOVATION AND TECHNOLOGY | 2006年 / 519-521卷
关键词：
aluminum alloy; conversion coatings; zinc phosphate; Mn2+ additive; photoelectron spectroscopy; scanning electron microscopy; Auger electron spectroscopy;
D O I：
10.4028/www.scientific.net/MSF.519-521.753
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The present work is part of a broader investigation of the effects of additives in zinc phosphate (ZPO) coating solutions that are designed for specific applications to Al and its alloys. ZPO conversion coatings improve the corrosion resistance of the Al substrate and increase the adhesion of paint. Coatings formed on 2024-T3 aluminum alloy, after dipping in ZPO coating baths containing Mn2+, have been studied by X-ray photoelectron spectroscopy (XPS), SEM, and scanning Auger microscopy (SAM). Variations are observed in coating morphology and composition as the amount of Mn2+ in the coating solution increases through the 0 to 2500 ppm range. Adhesion tests give information on the relative strength of the coating-substrate interaction at different microstructural areas.
引用
收藏
页码：753 / 758
页数：6
相关论文
共 50 条
  • [21] The effect of pH and role of Ni2+ in zinc phosphating of 2024-Al alloy.: Part I:: Macroscopic studies with XPS and SEM
    Akhtar, A. S.
    Wong, K. C.
    Mitchell, K. A. R.
    APPLIED SURFACE SCIENCE, 2006, 253 (02) : 493 - 501
  • [22] Microelectrochemical studies of pit initiation at single inclusions in Al 2024-T3
    Suter, T
    Alkire, RC
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2001, 148 (01) : B36 - B42
  • [23] Influence of Aerospace Standard Surface Pretreatment on the Intermetallic Phases and CeCC of 2024-T3 Al-Cu Alloy
    Jesus Alba-Galvin, Juan
    Gonzalez-Rovira, Leandro
    Bethencourt, Manuel
    Javier Botana, Francisco
    Maria Sanchez-Amaya, Jose
    METALS, 2019, 9 (03):
  • [24] Effect of Cro3 Sealing Time on Anodized Al 2024-T3
    Korda, Akhmad A.
    Hidayat, R. Z.
    6TH ASIAN PHYSICS SYMPOSIUM, 2016, 739
  • [25] Influence of pre-treatments on the surface condition of 2024-T3 aluminum alloy
    Pires, I.
    Quintino, L.
    Rangel, C.M.
    Thompson, G.E.
    Skeldon, P.
    Zhou, X.
    Transactions of the Institute of Metal Finishing, 2000, 78 (05): : 179 - 185
  • [26] Influence of pre-treatments on the surface condition of 2024-T3 aluminium alloy
    Pires, I
    Quintino, L
    Rangel, CM
    Thompson, GE
    Skeldon, P
    Zhou, X
    TRANSACTIONS OF THE INSTITUTE OF METAL FINISHING, 2000, 78 : 179 - 185
  • [27] Surface analysis of various methods of preparing Al 2024-T3 surfaces for painting
    De Rosa, RL
    Grant, JT
    Katsen, L
    Donley, M
    Bierwagen, GP
    CORROSION, 2000, 56 (04) : 395 - 400
  • [28] On the estimation of fatigue life in bolt clamped Al-alloy 2024-T3 plates
    Ghorbani, H.
    Chakherlou, T. N.
    Taghizadeh, H.
    ENGINEERING FRACTURE MECHANICS, 2016, 164 : 74 - 92
  • [29] Protection Mechanism of Al-Rich Epoxy Primer on Aluminum Alloy 2024-T3
    Wang, Xi
    Frankel, G. S.
    CORROSION, 2017, 73 (10) : 1192 - 1195
  • [30] Effect of Thickness on the Structure and Corrosion Performance of Sputtered Ce-Al-O Coatings on Al 2024-T3 Alloy Substrates
    Liu, Yuanyuan
    Huang, Jiamu
    Qin, Lilu
    Claypool, James B.
    O'Keefe, Matthew J.
    Jiang, Yiming
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2018, 165 (07) : C395 - C402
12345