Solidification cracking susceptibility of ferritic stainless steels using Modified Varestraint Transvarestraint (MVT) method

被引：2

作者：

Konadu, D. S. ^{[1
,2
]}

Pistorius, P. G. H. ^{[1
]}

Du Toit, M. ^{[3
]}

Griesche, Axel ^{[4
]}

机构：

[1] Univ Pretoria, Dept Mat Sci & Met Engn, ZA-0002 Pretoria, South Africa

[2] Univ Ghana, Dept Mat Sci & Engn, POB LG 77, Accra, Ghana

[3] Univ Wollongong, Sch Mech Mat Mechatron & Biomed Engn, Wollongong, NSW, Australia

[4] Fed Inst Mat Res & Testing, Bundesanstalt Materialforsch & Prufung BAM, Berlin, Germany

来源：

SADHANA-ACADEMY PROCEEDINGS IN ENGINEERING SCIENCES | 2019年 / 44卷 / 09期

关键词：

Modified Varestraint Transvarestraint; solidification cracking; ferritic stainless steel; microstructure; welding; susceptibility;

D O I：

10.1007/s12046-019-1175-0

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The Modified Varestraint Transvarestraint (MVT) test was used to investigate the solidification cracking susceptibility of an unstabilised, a Nb-stabilised and two (Ti + Nb) dual-stabilised ferritic stainless steels. Two different welding speeds of 6 and 3 mm/s using autogenous gas tungsten arc welding were employed. At the welding speed of 6 mm/s, the high-content (Ti + Nb) steel was resistant and the Nb-stabilised steel was marginally susceptible to solidification cracking. At the welding speed of 3 mm/s, the Nb and the high (Ti + Nb) steels were found to be marginally susceptible to solidification cracking while the unstabilised and low-content (Ti + Nb) grades were resistant to solidification cracking. The weld metal microstructures transverse to the welding direction revealed columnar grains in all the samples for both welding speeds. The ferritic stainless steels were generally resistant to solidification cracking, except the Nb-stabilised steel, which was marginally susceptible to solidification cracking.

引用

页数：6

共 50 条

[21] SOLIDIFICATION BEHAVIOR AND CRACKING SUSCEPTIBILITY OF PULSED-LASER WELDS IN AUSTENITIC STAINLESS-STEELS
LIPPOLD, JC
WELDING JOURNAL, 1994, 73 (06) : S129 - S139
[22] Prediction of solidification mode and hot cracking susceptibility in laser welds of high nitrogen stainless steels
Nishimoto, K
Mori, H
TRENDS IN WELDING RESEARCH, PROCEEDINGS, 2003, : 53 - 58
[23] Effects of ferrite content and concentrations of carbon and silicon on weld solidification cracking susceptibility of stainless steels
Kadoi, Kota
Ueno, Seiya
Inoue, Hiroshige
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2023, 25 : 1314 - 1321
[24] SOLIDIFICATION CRACKING IN THICK-WALLED TUBULAR WELDS AND APPLICATION OF THE MODIFIED TRANSVARESTRAINT TEST
MORRIS, GJ
METALS FORUM, 1980, 3 (03): : 167 - 174
[25] Effect of nitrogen and solidification mode on hot cracking susceptibility in laser welds of austenitic stainless steels
Nishimoto, K
Mori, H
FIRST INTERNATIONAL SYMPOSIUM ON HIGH-POWER LASER MACROPROCESSING, 2003, 4831 : 214 - 223
[26] EFFECTS OF COMPOSITION ON STRESS CORROSION CRACKING OF FERRITIC STAINLESS STEELS
BOND, AP
DUNDAS, HJ
CORROSION, 1968, 24 (10) : 344 - &
[27] Effect of solidification models on predicting susceptibility of carbon steels to solidification cracking
Soysal, Tayfun
WELDING IN THE WORLD, 2021, 65 (10) : 1943 - 1954
[28] Effect of solidification models on predicting susceptibility of carbon steels to solidification cracking
Tayfun Soysal
Welding in the World, 2021, 65 : 1943 - 1954
[29] Effect of solidification behaviour of austenitic stainless steel on the solidification cracking susceptibility
Liu, R. (lrp_msc@nuaa.edu.cn), 2005, China Welding (14):
[30] STUDY OF HOT CRACKING BEHAVIOUR OF NITROGEN-ENHANCED AUSTENITIC STAINLESS STEELS USING VARESTRAINT AND HOT DUCTILITY TESTS
Srinivasan, Ganesan
Divya, Murthy
Albert, Shaju K.
Bhaduri, Arun Kumar
Klenk, Andreas
Achar, D. R. Gopalakrishna
WELDING IN THE WORLD, 2010, 54 (11-12) : R322 - R332

← 1 2 3 4 5 →