The durability of jute fibre-reinforced phenolic composites

被引：88
|
作者：
Singh, B [1 ]
Gupta, M [1 ]
Verma, A [1 ]
机构：
[1] Cent Bldg Res Inst, Roorkee 247667, Uttar Pradesh, India
来源：
COMPOSITES SCIENCE AND TECHNOLOGY | 2000年 / 60卷 / 04期
关键词：
polymer-matrix composites; environmental degradation; scanning electron microscopy (SEM); jute fibres; fungal infestation;
D O I：
10.1016/S0266-3538(99)00172-4
中图分类号：
TB33 [复合材料];
学科分类号：
摘要：
The physical and mechanical properties of jute composites have been studied under various humidity, hydrothermal and weathering conditions. The aging-induced deteriorative effect of these conditions on the dimensional stability, surface topography and mechanical properties of the composites was observed. The severity of aging was more detrimental in an accelerated water test as compared to the other exposure conditions. SEM observation reveals the fibre accentuation along with fibre breakage/splitting and surface discoloration in both natural and accelerated weathering of UV exposure. Some biological defacement in the form of fungal infestation appeared at the cut edges of weathered composites while extensive disfigurement was noticed on all surfaces under high humidity/-water-immersion. These results could be useful as an indicator for assessing the suitability of jute composites in damp and dry conditions. (C) 2000 Elsevier Science Ltd. All rights reserved.
引用
收藏
页码：581 / 589
页数：9
相关论文
共 50 条
  • [21] Durability aspects of fibre reinforced composites
    Bhide, SJ
    Zurale, MM
    DURABILITY OF BUILDING MATERIALS AND COMPONENTS 8, VOLS 1-4, PROCEEDINGS, 1999, : 1382 - 1391
  • [22] Effect of Rate of Loading on Jute Fibre-Reinforced Polymer Composite
    Pawan Kumar
    Manvendra Tiwari
    Mamookho Elizabeth Makhatha
    Abhijit Dey
    Bipin Bihari Verma
    Transactions of the Indian Institute of Metals, 2020, 73 : 1573 - 1577
  • [23] Mechanical properties and durability of jute reinforced thermosetting composites
    Sahoo, S.
    Nakai, A.
    Kotaki, M.
    Ishiaku, U. S.
    Mohanty, A. K.
    Misra, M.
    Hamada, H.
    JOURNAL OF BIOBASED MATERIALS AND BIOENERGY, 2007, 1 (03) : 427 - 436
  • [24] Investigations on jute fibre-reinforced polyester composites: Effect of alkali treatment and poly(lactic acid) coating
    Gupta, M. K.
    JOURNAL OF INDUSTRIAL TEXTILES, 2020, 49 (07) : 923 - 942
  • [25] Effect of hybridization and composite architecture symmetry in the bonded joint performance of jute/carbon fibre-reinforced composites
    de Queiroz, H. F. M.
    Pastor, V.
    de Mendonca, A. C.
    Neto, J. S. S.
    Cavalcanti, D. K. K.
    Banea, M. D.
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2024, 133
  • [26] Designing with fibre-reinforced composites: Advantages and pitfalls
    Ellyin, F
    TRENDS IN STRUCTURAL MECHANICS: THEORY, PRACTICE, EDUCATION, 1997, 54 : 67 - 74
  • [27] Squeezing flow of continuous fibre-reinforced composites
    Goshawk, JA
    Navez, VP
    Jones, RS
    JOURNAL OF NON-NEWTONIAN FLUID MECHANICS, 1997, 73 (03) : 327 - 342
  • [28] Manufacturing defects in fibre-reinforced plastics composites
    Summerscales, J.
    Insight: Non-Destructive Testing and Condition Monitoring, 1994, 36 (12): : 936 - 942
  • [29] Durability of fibre-reinforced cementitious composites (FRCC) including recycled synthetic fibres and rubber aggregates
    Signorini, Cesare
    Nobili, Andrea
    APPLICATIONS IN ENGINEERING SCIENCE, 2022, 9
  • [30] Textile preforms for tungsten fibre-reinforced composites
    Gietl, H.
    von Mueller, A.
    Coenen, J. W.
    Decius, M.
    Ewert, D.
    Hoeschen, T.
    Huber, Ph
    Milwich, M.
    Riesch, J.
    Neu, R.
    JOURNAL OF COMPOSITE MATERIALS, 2018, 52 (28) : 3875 - 3884
12345