Parametric Optimization of Friction Stir Welding of Dissimilar Al 5083 and Al 6061 Alloys by Using Taguchi Method

Friction stir welding is a promising technique for joining the dissimilar metals for applications in aerospace, automobile, defense and shipbuilding. In the present study, friction stir welding (FSW) processing parameter for dissimilar joint Al 5083 alloy and Al 6061 alloy were investigated. The FSW welding parameters investigated are rotational speed (600 rpm, 865 rpm and 1140 rpm), tilt angle (1 degrees, 2 degrees and 3 degrees) and number of pass (1, 2 and 4). Taguchi teclmique L9 orthogonal array was applied to determine the optimize control factors which will yield better tensile strength of FSW dissimilar joint Al 5083-Al 6061 alloy. The effects of the process parameters on response characteristics (tensile strength and microhardness) were studied. The finest grain size is observed in the weld nugget zone compared to other region. Based on S/N response for tensile strength the optimum parameters are 600 rpm rotational speed, 1 tilt angle and 2 number of passes, respectively. The different welding parameters influenced the tensile properties and microhardness which largely dependent on the flow of metal in the joint. At 600 rpm rotational speed shows the highest tensile strength 162.37 MPa as compared to 865 rpm and 1140 rpm due to sufficient material flow to promote the joining. While, the tilt angle of showed the best strength because it might have optimal contact between the tool pin and specimens. In addition, 2 number of pass have the highest tensile strength because grains underwent plastic deformation and thermal exposure which lead to significant grain refinement.