Microwave sintering of 8 mol% yttria-zirconia (8YZ): An inert matrix material for nuclear fuel applications

被引：16

作者：

Thridandapani, R. R. ^{[1
]}

Folgar, C. E. ^{[1
]}

Folz, D. C. ^{[1
]}

Clark, D. E. ^{[1
]}

Wheeler, K. ^{[2
]}

Peralta, P. ^{[2
]}

机构：

[1] Virginia Polytech Inst & State Univ, Dept Mat Sci & Engn, Blacksburg, VA 24061 USA

[2] Arizona State Univ, Tempe, AZ 85287 USA

来源：

JOURNAL OF NUCLEAR MATERIALS | 2009年 / 384卷 / 02期

关键词：

TRANSMUTATION; ALUMINA; POWDER;

D O I：

10.1016/j.jnucmat.2008.11.010

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

This study focused on reducing overall processing time and temperature for fully stabilized zirconia, an inert matrix material candidate, to minimize the loss of actinides (that will be incorporated into the matrix material), while maintaining at least 90% theoretical density (TD). The effects of different processing routes on bulk density and microstructure were evaluated. The results obtained by adopting microwave sintering for 8 mol% Y2O3-ZrO2 were compared to conventional sintering. A 20 min soak time at 1300 degrees C resulted in pellets with 90% TD for microwave-processed samples, compared to 77% TD for pellets processed conventionally. A similar density was obtained at lower temperature (1200 degrees C) by increasing the soak time to 100 min in microwave processing. This time and temperature resulted in 60% TD conventionally processed pellets. Compressive strength values obtained for a 1300 degrees C (20 min soak time) microwave-processed sample were higher (1600 MPa) as compared to a conventionally processed sample (1300 MPa). (C) 2008 Elsevier B.V. All rights reserved.

引用

页码：153 / 157

页数：5