Application of a new ultrasonic-assisted semi-solid brazing on dissimilar Al/Mg alloys

被引：20
|
作者：
Xu, Zhiwu [1 ]
Li, Zhengwei [1 ]
Peng, Bo [1 ]
Ma, Zhipeng [1 ]
Yan, Jiuchun [1 ]
机构：
[1] Harbin Inst Technol, State Key Lab Adv Welding & Joining, Harbin 150001, Heilongjiang, Peoples R China
来源：
MATERIALS LETTERS | 2018年 / 228卷
基金：
美国国家科学基金会;
关键词：
Ultrasonic; Semi-solid brazing; Intermetallic compound; Microstructure; Diffusion; Cavitation; AL-ALLOY; MG; MAGNESIUM;
D O I：
10.1016/j.matlet.2018.05.131
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In this work, an ultrasonic-assisted semi-solid brazing method was proposed to join Al/Mg. Oxide films on substrate surfaces can be successfully removed even when filler metal was at semi-solid state. A large quantity of intermetallic compounds (IMCs) formed at 460 degrees C because of large amount of Al and Mg dissolved into joint caused by strong cavitation. Decreasing the temperature to 430 degrees C could significantly reduce IMC. However, weak cavitation happened inside low liquid phase fraction at 420 degrees C, making it difficult to break IMCs and solid phases. (C) 2018 Elsevier B.V. All rights reserved.
引用
收藏
页码：72 / 76
页数：5
相关论文
共 50 条
  • [31] A formalism for predicting ultrasonic properties of alloys in a semi-solid state
    Niessner, AF
    Gordon, GA
    REVIEW OF PROGRESS IN QUANTITATIVE NONDESTRUCTIVE EVALUATION, VOLS 17A AND 17B, 1998, : 1855 - 1861
  • [32] RHEOLOGICAL BEHAVIOUR OF SEMI-SOLID MG-Y ALLOYS
    Peng, Qiuming
    Huang, Yuanding
    Hort, Norbert
    Kainer, Karl Ulrich
    MAGNESIUM TECHNOLOGY 2010, 2010, : 329 - 332
  • [33] Semi-solid forming using strain-introduced Mg-Al based alloys
    Kamado, S
    Kojima, Y
    PROCEEDINGS OF THE THIRD INTERNATIONAL MAGNESIUM CONFERENCE, 1997, : 123 - 136
  • [34] High temperature strength of semi-solid formed Mg-Zn-Al-Ca alloys
    Rudi, Rachmat Suhardi
    Kamado, Shigeharu
    Ikeya, Naoyuki
    Araki, Tomomi
    Kojima, Yo
    Materials Science Forum, 2000, 350 : 79 - 84
  • [35] Microstructure and mechanical properties of cast and semi-solid formed Mg-Al-Zn alloys
    Kim, Jeong-Min
    Park, Bong-Koo
    Jun, Joong-Hwan
    Kim, Ki-Tae
    Jung, Woon-Jae
    SEMI-SOLID PROCESSING OF ALLOYS AND COMPOSITES, 2006, 116-117 (288-291): : 288 - 291
  • [36] Mechanical properties and microstructure of semi-solid injection molded Mg-Al-Ca alloys
    Sakamoto, Kazuo
    Yamamoto, Kenichi
    Keikinzoku/Journal of Japan Institute of Light Metals, 2002, 52 (10): : 437 - 441
  • [37] Microstructure Evolution of Ultrasonic-Assisted Electrical Resistance Brazing Joints of 6063 Aluminum Alloys
    Yu Weiyuan
    Wu Weijie
    Sun Xuemin
    RARE METAL MATERIALS AND ENGINEERING, 2019, 48 (12) : 4081 - 4087
  • [38] Control Al/Mg intermetallic compound formation during ultrasonic-assisted soldering Mg to Al
    Xu, Zhiwu
    Li, Zhengwei
    Li, Jiaqi
    Ma, Zhipeng
    Yan, Jiuchun
    ULTRASONICS SONOCHEMISTRY, 2018, 46 : 79 - 88
  • [39] Joint formation and mechanical properties of ultrasonic-assisted transient liquid bonding of dissimilar Al/Mg with a Zn interlayer in air
    Liu, Xuesong
    Li, Zhengwei
    Xu, Zhiwu
    Chen, Shu
    Peng, Liming
    Yan, Jiuchun
    JOURNAL OF MANUFACTURING PROCESSES, 2022, 77 : 632 - 641
  • [40] Degassing effect of ultrasonic vibration in molten melt and semi-solid slurry of Al-Si alloys
    Wu Shusen Liu Longfei Ma Qianqian Mao Youwu and An Ping State Key Lab of Materials Processing and Die Mould Technology Huazhong University of Science and Technology Wuhan China
    China Foundry, 2012, 9 (03) : 201 - 206
12345