Accelerated hygrothermal aging of Talc/Cycloaliphatic epoxy composites

被引：5
|
作者：
Tomasi, Julie M. [1 ]
Krieg, Aaron S. [1 ]
Jensen, Nicholas J. [2 ]
Miskioglu, Ibrahim [2 ]
King, Julia A. [1 ]
Odegard, Gregory M. [2 ]
机构：
[1] Michigan Technol Univ, Dept Chem Engn, Houghton, MI 49931 USA
[2] Michigan Technol Univ, Dept Mech Engn, Engn Mech, Houghton, MI 49931 USA
来源：
POLYMER COMPOSITES | 2019年 / 40卷 / 07期
基金：
美国国家科学基金会;
关键词：
PERFORMANCE; TALC;
D O I：
10.1002/pc.25131
中图分类号：
TB33 [复合材料];
学科分类号：
摘要：
Cycloaliphatic epoxy (CE) systems are resistant to many aging mechanisms, which make them useful in applications with harsh environments. Reinforcement has been used in epoxy systems to decrease water absorption and improve aging resistance; thus, it is expected that talc would benefit CE systems in a similar manner. Neat, 10, and 20 wt% talc/CE composites were aged at 50 degrees C and 100% relative humidity for up to 398 hr. Three-point bend testing and dynamic mechanical analysis were performed on the aged and unaged samples. Talc reduced the amount of water absorbed in the composites significantly, and increased the composite flexural stiffness at all aging levels. Talc does not appear to mitigate the negative effects of aging on flexural strength or glass transition temperature (T-g). POLYM. COMPOS., 40:2946-2953, 2019. (c) 2018 Society of Plastics Engineers
引用
收藏
页码：2946 / 2953
页数：8
相关论文
共 50 条
  • [21] The Effect of Hygrothermal Aging on the Properties of Epoxy Resin
    Wang, Youyuan
    Liu, Yu
    Xiao, Kun
    Wang, Can
    Zhang, Zhanxi
    [J]. JOURNAL OF ELECTRICAL ENGINEERING & TECHNOLOGY, 2018, 13 (02) : 892 - 901
  • [22] Electrical Tracking in Cycloaliphatic Epoxy Based Nanostructured Composites
    Guastavino, F.
    Thelakkadan, A. S.
    Coletti, G.
    Ratto, A.
    [J]. CEIDP: 2009 ANNUAL REPORT CONFERENCE ON ELECTRICAL INSULATION AND DIELECTRIC PHENOMENA, 2009, : 600 - 603
  • [23] Effect of hygrothermal aging on polyetherimide composites
    Arici, Aziz Armagan
    [J]. JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 2007, 26 (18) : 1937 - 1942
  • [24] Accelerated hygrothermal cyclical tests for carbon/epoxy laminates
    Jedidi, J
    Jacquemin, F
    Vautrin, A
    [J]. COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2006, 37 (04) : 636 - 645
  • [25] Study of Hygrothermal Aging for Basalt Fiber/Epoxy Resin Composites Modified with CeCl3
    Li, Chong
    Zhang, Longwang
    Wang, Haoyu
    Song, Yiguo
    Wang, Jiayou
    [J]. POLYMERS, 2024, 16 (06)
  • [26] Multiscale modeling of mechanical behaviors of carbon fiber reinforced epoxy composites subjected to hygrothermal aging
    Guo, Fang-Liang
    Huang, Pei
    Li, Yuan-Qing
    Hu, Ning
    Fu, Shao-Yun
    [J]. COMPOSITE STRUCTURES, 2021, 256
  • [27] Study on the mechanical properties of nanoclay-epoxy composites under different hygrothermal aging conditions
    Shettar, Manjunath
    Kini, U. Achutha
    Sharma, Sathyashankara
    Hiremath, Pavan
    Gowrishankar, M. C.
    [J]. MATERIALS RESEARCH EXPRESS, 2019, 6 (08)
  • [28] Effect of hygrothermal aging on the diffusion of seawater in epoxy/glass composites studied by positron lifetime spectroscopy
    Radha, J. C.
    Ranganathaiah, C.
    [J]. POLYMER COMPOSITES, 2008, 29 (02) : 149 - 155
  • [29] Using machine learning and experimental study to correlate and predict accelerated aging with natural aging of GFRP composites in hygrothermal conditions
    Wang, Jing
    Karimi, Sajjad
    Zeinalzad, Parastoo
    Zhang, Jingyu
    Gong, Zhi
    [J]. CONSTRUCTION AND BUILDING MATERIALS, 2024, 438
  • [30] The hygrothermal aging process and mechanism of the novolac epoxy resin
    Wang, Man
    Xu, Xiaowei
    Ji, Jin
    Yang, Yang
    Shen, Jianfeng
    Ye, Mingxin
    [J]. COMPOSITES PART B-ENGINEERING, 2016, 107 : 1 - 8
12345