Effect of dopants on the fracture toughness of silicon

被引：13

作者：

Swadener, JG ^{[1
]}

Nastasi, M ^{[1
]}

机构：

[1] Los Alamos Natl Lab, Los Alamos, NM 87545 USA

来源：

JOURNAL OF MATERIALS SCIENCE LETTERS | 2002年 / 21卷 / 17期

关键词：

D O I：

10.1023/A:1019772717743

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Fracture experiments were conducted on p-type and n-type Si in the presence and absence of hydrogen. It was found that fracture toughness is slightly less than the fracture toughness of n-type silicon. Annealing silicon in an Ar/H2 atmosphere gave a hydrogen concentration of less than 0.1 ppm, which did not have any measurable effect on fracture toughness. Likewise, the exposure of pre-cracked specimens to H2 did not cause any measurable change in fracture toughness.

引用

页码：1363 / 1365

页数：3

共 50 条

[31] Fracture toughness of austempered high silicon cast steel
Chen, X
Li, YX
Fu, HG
ACTA METALLURGICA SINICA, 2005, 41 (10) : 1061 - 1065
[32] FRACTURE-TOUGHNESS MEASUREMENTS ON SILICON-CARBIDE
HIMSOLT, G
FETT, T
KELLER, K
MUNZ, D
MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK, 1989, 20 (05) : 148 - 153
[33] DYNAMIC FRACTURE-TOUGHNESS OF SILICON-NITRIDE
KOBAYASHI, AS
EMERY, AF
LIAW, BM
AMERICAN CERAMIC SOCIETY BULLETIN, 1981, 60 (09): : 926 - 926
[34] Fracture toughness measurement of thin-film silicon
Ando, T
Li, S
Nakao, S
Kasai, T
Tanaka, H
Shikida, M
Sato, K
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2005, 28 (08) : 687 - 694
[35] VAMAS round robin on fracture toughness of silicon nitride
Mizuno, M.
Okuda, H.
1793, American Ceramic Soc, Westerville, OH, United States (78)
[36] Fracture toughness and subcritical crack growth in polycrystalline silicon
Chasiotis, I.
Cho, S. W.
Jonnalagadda, K.
JOURNAL OF APPLIED MECHANICS-TRANSACTIONS OF THE ASME, 2006, 73 (05): : 714 - 722
[37] Fracture toughness and crack bridging of a silicon nitride ceramic
Maniette, Y.
Inagaki, M.
Sakai, M.
Journal of the European Ceramic Society, 1991, 7 (04) : 255 - 263
[38] Short-Crack Fracture Toughness of Silicon Carbide
Kaur, Sarbjit
Cutler, Raymond A.
Shetty, Dinesh K.
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2009, 92 (01) : 179 - 185
[39] Fracture toughness of polycrystalline silicon carbide thin films
Bellante, JJ
Kahn, H
Ballarini, R
Zorman, CA
Mehregany, M
Heuer, AH
APPLIED PHYSICS LETTERS, 2005, 86 (07) : 1 - 3
[40] The effect of dopants on silicon surface chemistry.
Crowell, JE
Jacobson, ML
Wang, DJ
Batinica, GJ
Ning, BMH
Chiu, MC
ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 1997, 213 : 216 - COLL

← 1 2 3 4 5 →