Effect of graphite degradation on the LCF properties of nodular cast iron

被引：0
|
作者：
Denk, Josef [1 ]
机构：
[1] ABB Turbo Syst, Dev Dept ZTE, CH-5401 Baden, Switzerland
来源：
FDMD II - JIP 2014 - FATIGUE DESIGN & MATERIAL DEFECTS | 2014年 / 12卷
关键词：
D O I：
10.1051/matecconf/20141204001
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The effect of degraded microstructure on the tensile and LCF properties was studied on a casing of a turbocharger, which exhibited locally irregular graphite formation. The tensile tests showed that the ductility values of the zone with degraded graphite decreased strongly compared to the zone with normal graphite, while the strength values decreased only slightly. Based on these results and a LCF reference curve for nodular cast iron with normal graphite structure, a synthetic LCF curve was generated for the material condition with degraded graphite structure. LCF tests on specimens with irregular graphite structure confirmed the predicted LCF behaviour quite good.
引用
收藏
页数：3
相关论文
共 50 条
  • [41] Surface modification of nodular cast iron: A comparative study on graphite elimination
    Karamis, M. B.
    Yildizli, K.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 527 (20): : 5225 - 5229
  • [42] CONTRIBUTION TO STUDY OF NODULAR GRAPHITE NUCLEI IN CAST IRON FOR INGOT MOULDS
    POYET, P
    PONCHON, J
    FONDERIE-FRANCE, 1969, (277): : 183 - &
  • [43] LASER SURFACE MELTING TREATMENT OF NODULAR GRAPHITE CAST IRON.
    Xie Shum-ing
    Fan Yi
    Huang Man-hui
    Jinshu Rechuli/Heat Treatment of Metals, 1987, (11): : 19 - 23
  • [44] SECONDARY GRAPHITE FORMATION IN TEMPERED NODULAR CAST-IRON WELDMENTS
    ASKELAND, DR
    BIRER, N
    WELDING JOURNAL, 1979, 59 (11) : S337 - S342
  • [45] SECONDARY GRAPHITE FORMATION IN TEMPERED NODULAR CAST IRON WELDMENTS.
    Askeland, D.R.
    Birer, N.
    Welding Journal (Miami, Fla), 1979, 58 (11):
  • [46] Long-life multiaxial fatigue of a nodular graphite cast iron
    Marquis, GB
    Karjalafnen-Roikonen, P
    BIAXIAL/MULTIAXIAL FATIGUE AND FRACTURE, 2003, 31 : 105 - 122
  • [47] Effects of ferrite and graphite phases on scratch characteristics of nodular cast iron
    Xu, Zhitong
    Liu, Ming
    Gao, Chenghui
    Yang, Fuqian
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2024, 30 : 2257 - 2263
  • [48] Influence of distribution and size of graphite particle on the machinability of nodular cast iron
    Yang, H. W.
    Wang, X. M.
    Liu, W.
    Huang, W.
    Wu, M.
    Xue, M. L.
    Li, L.
    ENGINEERING FRACTURE MECHANICS, 2024, 297
  • [49] NODULAR CAST IRON
    FONTANA, MG
    INDUSTRIAL AND ENGINEERING CHEMISTRY, 1950, 42 (01): : A67 - A68
  • [50] LOW TEMPERATURE TENSILE PROPERTIES OF NODULAR GRAPHITE CAST IRONS
    RICKARDS, PJ
    CRYOGENICS, 1969, 9 (06) : 465 - &
12345