Hydration and microstructure of nano-clay cement material in ion erosion solution

被引：12
|
作者：
Hong, Zi-jie [1 ]
Zuo, Jian-ping [1 ,2 ]
Liu, Chang [1 ]
Zhang, Zi-shan [1 ]
机构：
[1] China Univ Min & Technol, Sch Mech & Civil Engn, Beijing 100083, Peoples R China
[2] China Univ Min & Technol, State Key Lab Coal Resources & Safe Min, Beijing 100083, Peoples R China
来源：
MATERIALS LETTERS | 2019年 / 252卷
基金：
中国国家自然科学基金;
关键词：
FTIR; Hydration; Microstructure; Ion solution;
D O I：
10.1016/j.matlet.2019.05.085
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The influence of nano-clay (NC) content on the hydration and microstructure of cement grouting material was investigated under sodium chloride solution. Five different NC cement pastes were prepared and studied by means of FT-IR, TG-DTG and SEM analysis. The results indicated that NC promoted the formation of the hydrate ettringite (AFt), and made the AFt transform from loose acicular into cylindrical shape of staggered reticulated skeleton structure. Besides, with the increase of NC content, calcium silicate hydrate (C-S-H) gel increased and the calcium hydroxide (CH) decreased, NC obviously reduced the porosity and made an increasingly dense microstructure. However, when the content of NC is more than 3 wt%, the hydration process is inhibited, and the effect of ion erosion resistance is still better than without NC. The results of compressive strength and chloride ion diffusion coefficient are better verified by microstructure. (C) 2019 Elsevier B.V. All rights reserved.
引用
收藏
页码：27 / 30
页数：4
相关论文
共 50 条
  • [21] Morphology and Strength Of Cement Paste from Clay as Nano material
    Norhasri, Muhd M. S.
    Hamidah, M. S.
    Fadzil, Mohd A.
    MECHANICAL DESIGN AND POWER ENGINEERING, PTS 1 AND 2, 2014, 490-491 : 19 - 24
  • [22] Effect of Nano-SiO2 on the Hydration and Microstructure of Portland Cement
    Wang, Liguo
    Zheng, Dapeng
    Zhang, Shupeng
    Cui, Hongzhi
    Li, Dongxu
    NANOMATERIALS, 2016, 6 (12)
  • [23] Effect of nano-silica on the hydration and microstructure of grey and white cement
    Zhang, Ai
    Ge, Yong
    MAGAZINE OF CONCRETE RESEARCH, 2020, 72 (12) : 634 - 648
  • [24] Mechanisms behind injecting the combination of nano-clay particles and polymer solution for enhanced oil recovery
    Seyyed Shahram Khalili Nezhad
    Goshtasp Cheraghian
    Applied Nanoscience, 2016, 6 : 923 - 931
  • [25] Mechanisms behind injecting the combination of nano-clay particles and polymer solution for enhanced oil recovery
    Nezhad, Seyyed Shahram Khalili
    Cheraghian, Goshtasp
    APPLIED NANOSCIENCE, 2016, 6 (06) : 923 - 931
  • [26] Hydration process and microstructure of magnesium potassium phosphate cement with nitrate solution
    Yan Tao
    Lai Zhenyu
    Wang Yuanyuan
    He Xin
    Wu Jie
    Lu Zhongyuan
    Lv Shuzhen
    Li Feng
    Fan Xiaoling
    Zhang Haibin
    SCIENCE OF THE TOTAL ENVIRONMENT, 2020, 703
  • [27] Hydration characteristic, thermal expansion and microstructure of cement containing nano-silica
    Abd El Aleem, S.
    Heikal, Mohamed
    Morsi, W. M.
    CONSTRUCTION AND BUILDING MATERIALS, 2014, 59 : 151 - 160
  • [28] The hydration, microstructure, and mechanical properties of vaterite calcined clay cement (VC3)
    Li, Yaqiang
    Li, Yue
    Ma, Hongyan
    Li, Jiaqi
    CEMENT AND CONCRETE RESEARCH, 2024, 175
  • [29] Influence of temperature on hydration and microstructure properties of limestone-calcined clay blended cement
    Geetika Mishra
    Arun C. Emmanuel
    Shashank Bishnoi
    Materials and Structures, 2019, 52
  • [30] Influence of temperature on hydration and microstructure properties of limestone-calcined clay blended cement
    Mishra, Geetika
    Emmanuel, Arun C.
    Bishnoi, Shashank
    MATERIALS AND STRUCTURES, 2019, 52 (05)
12345