Technical features evaluation of an alumina powder prepared by combustion synthesis

被引：0
|
作者：
Tavares, A. P. [1 ]
Olhero, S. M. [1 ]
Ferreira, J. M. F. [1 ]
机构：
[1] Univ Aveiro, CICECO, Ceram & Glass Engn Dept, P-3810193 Aveiro, Portugal
来源：
ADVANCED MATERIALS FORUM III, PTS 1 AND 2 | 2006年 / 514-516卷
关键词：
alumina; combustion synthesis; colloidal processing; sintering;
D O I：
10.4028/www.scientific.net/MSF.514-516.1546
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
This work aims at characterising an alumina powder obtained by combustion synthesis, and at evaluating the technical properties of sintered bodies. Particle size distribution and XRD were used to characterise the alumina powder; electrophoresis and rheological measurements were used to select the most suitable processing conditions. Sintered density, flexural strength, Vickers hardness and SEM analysis were used to characterise the bodies sintered at 1600 degrees C. The experimental results showed that a density of 3.60 g/cm(3) could be obtained in absence of sintering aids and that the sintered bodies exhibited a flexural strength of 220 MPa and a Vickers hardness of 1100.
引用
收藏
页码：1546 / 1550
页数：5
相关论文
共 50 条
  • [41] ATTRITION AND METALS RESISTANT FCC CATALYST PREPARED WITH ALUMINA POWDER IN THE MATRIX
    LOWE, JA
    MATOCHA, CK
    PEDERSEN, LA
    ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 1988, 196 : 60 - PETR
  • [42] Heterocoagulation moulding of alumina powder suspensions prepared using citrate dispersant
    Prabhakaran, K.
    Sooraj, R.
    Kumbhar, C. S.
    Melkeri, A.
    Gokhale, N. M.
    Sharma, S. C.
    CERAMICS INTERNATIONAL, 2010, 36 (01) : 1 - 8
  • [43] Evaluation of Pd/alumina catalysts, produced by combustion synthesis, in the ethanol oxidation reaction to acetic acid
    School of Chemistry, Federal University of Rio de Janeiro, 21910 Rio de Janeiro-RJ, Brazil
    不详
    不详
    不详
    不详
    Appl Catal A Gen, 1-2 (87-92):
  • [44] Evaluation of Pd/alumina catalysts, produced by combustion synthesis, in the ethanol oxidation reaction to acetic acid
    Greca, MC
    Moraes, C
    Morelli, MR
    Segadaes, AM
    APPLIED CATALYSIS A-GENERAL, 1999, 179 (1-2) : 87 - 92
  • [45] Combustion process in the synthesis of electronic ceramic powder
    de Sousa, VC
    de Oliveira, CR
    Rodrigues, ACM
    Morelli, MR
    Kiminami, RHGA
    ADVANCED POWDER TECHNOLOGY II, 2001, 189-1 : 3 - 8
  • [46] Combustion synthesis of gadolinia doped ceria powder
    Mahata, T.
    Das, G.
    Mishra, R.K.
    Sharma, B.P.
    Journal of Alloys and Compounds, 2005, 391 (1-2): : 129 - 135
  • [47] Technical Evaluation of Recycling Powder From EAF
    Lopes O, Silva Leonardo
    Santos de, Assis Joao Batista
    de Mendonca, Cordeiro Fabricio C.
    Santos, Assis Paulo
    JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2009, 16 : 433 - 436
  • [48] Synthesis of alumina powder by the urea-glycine-nitrate combustion process: a mixed fuel approach to nanoscale metal oxides
    Sharma, Amit
    Rani, Amita
    Singh, Ajay
    Modi, O. P.
    Gupta, Gaurav K.
    APPLIED NANOSCIENCE, 2014, 4 (03) : 315 - 323
  • [49] Combustion synthesis of gadolinia doped ceria powder
    Mahata, I
    Das, G
    Mishra, RK
    Sharma, BP
    JOURNAL OF ALLOYS AND COMPOUNDS, 2005, 391 (1-2) : 129 - 135
  • [50] Combustion synthesis of ultrafine tungsten carbide powder
    Won H.I.
    Nersisyan H.H.
    Won C.W.
    J Mater Res, 2008, 9 (2393-2397): : 2393 - 2397
12345