Damage rate dependence of defect cluster nucleation in tungsten during irradiation

被引：4

作者：

Yamamoto, Y. ^{[1
]}

Yoshimatsu, J. ^{[1
]}

Morishita, K. ^{[2
]}

机构：

[1] Kyoto Univ, Grad Sch Energy Sci, Kyoto 6110011, Japan

[2] Kyoto Univ, Inst Adv Energy, Kyoto 6110011, Japan

来源：

JOURNAL OF NUCLEAR MATERIALS | 2013年 / 442卷 / 1-3期

关键词：

VOIDS;

D O I：

10.1016/j.jnucmat.2013.04.014

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Kinetic Monte-Carlo simulations were performed to investigate the damage rate (dpa/s) dependence of void nucleation in tungsten during irradiation. Simulation results indicated that, at temperatures where vacancies can move easily, the void nucleation rate decreases with increasing temperature due to the thermal instability of voids. At relatively high temperatures, no voids were observed unless the damage rate was high enough to nucleate them. (C) 2013 Elsevier B.V. All rights reserved.

引用

页码：S773 / S775

页数：3

共 50 条

[21] ENERGY DEPENDENCE OF ELECTRON DAMAGE IN TUNGSTEN
DICARLO, JA
STANLEY, JT
BULLETIN OF THE AMERICAN PHYSICAL SOCIETY, 1971, 16 (03): : 317 - &
[22] ENERGY DEPENDENCE OF RADIATION DAMAGE IN TUNGSTEN
MUSS, DR
TOWNSEND, JR
JOURNAL OF APPLIED PHYSICS, 1961, 32 (02) : 189 - &
[23] PROBLEMS ASSOCIATED WITH PRIMARY DAMAGE AND SECONDARY DEFECT NUCLEATION UNDER FUSION-REACTOR IRRADIATION CONDITIONS
HAYNS, MR
BULLETIN OF THE AMERICAN PHYSICAL SOCIETY, 1980, 25 (03): : 404 - 404
[24] The dependence of homogeneous nucleation rate on supersaturation
Girshick, Steven L.
JOURNAL OF CHEMICAL PHYSICS, 2014, 141 (02):
[25] POTENTIAL DEPENDENCE OF RATE OF NUCLEATION IN ELECTROCRYSTALLISATION
ARMSTRONG, RD
JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 1971, 29 (02) : 439 - +
[26] PRECIPITATE NUCLEATION DURING IRRADIATION
RUSSELL, KC
JOURNAL OF METALS, 1980, 32 (08): : 57 - 57
[27] Target depth dependence of damage rate in metals by 150 MeV proton irradiation
Yoshiie, T.
Ishi, Y.
Kuriyama, Y.
Mori, Y.
Sato, K.
Uesugi, T.
Xu, Q.
NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 2015, 342 : 166 - 169
[28] Recovery and accumulation of ion irradiation damage leading to dose rate dependence in GaAs
Kanayama, Toshihiko
JAPANESE JOURNAL OF APPLIED PHYSICS, 2020, 59 (09)
[29] A model calculation for irradiation rate dependence of defect structure in Fe-Cu alloy
Yanagita, S
Yoshiie, T
Ino, H
JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2000, 64 (02) : 115 - 124
[30] Direct observation of defect-mediated cluster nucleation
U. Kaiser
D.A. Muller
J.L. Grazul
A. Chuvilin
M. Kawasaki
Nature Materials, 2002, 1 : 102 - 105

← 1 2 3 4 5 →