Blends of syndiotactic polystyrene with SEBS triblock copolymers

Blending of styrene-b-(ethylene-co-1-butene)-b-styrene (SEBS) triblock copolymers with syndiotactic polystyrene (PSsyn) has been performed in a Brabender mixer above the higher glass transition temperature of the triblock copolymer but below the PSsyn melting point. The large excess of the triblock copolymer over the homopolymer as well as the significant amount of plasticized amorphous PSsyn phase allowed the easy processing under the used temperature conditions with good inter-face compatibility. The consequent interfacial adhesion between the amorphous PS phase and the unmelted PSsyn crystallites affects both the final morphology of the blend as well as its dynamic behavior. Indeed, such solid particles act as reinforcing point of the overall blend structure, as evidenced by scanning electron microscopy. Moreover, they contribute to a T-g increase in the order of 20 degreesC with respect to pure SEBS and to an appreciable conservation of mechanical proper-ties at temperatures higher than the T-g of the PS blocks of SEBS. The mechanical and thermal behavior of the synthesized blends has been studied and tentatively correlated to the molecular weight ratio between PSsyn and the PS blocks of SEBS. (C) 2002 Elsevier Science Ltd. All rights reserved.