Electrochemical production of Al-Sc alloy in CaCl2-Sc2O3 molten salt

被引：52

作者：

Harata, Masanori ^{[2
]}

Yasuda, Kouji ^{[1
]}

Yakushiji, Hiromasa ^{[3
]}

Okabe, Toru H. ^{[1
]}

机构：

[1] Univ Tokyo, Inst Ind Sci, Meguro Ku, Tokyo 1538505, Japan

[2] Univ Tokyo, Dept Mat Engn, Grad Sch Engn, Bunkyo Ku, Tokyo 1138656, Japan

[3] Pacific Metals Co Ltd, Tech Res & Dev Dept, Prod Div, Aomori 0318617, Japan

来源：

JOURNAL OF ALLOYS AND COMPOUNDS | 2009年 / 474卷 / 1-2期

关键词：

Scandium; Al-Sc alloy; Molten salt; Electrolysis; SOLID SOLUBILITY; REDUCTION; SCANDIUM; RESISTIVITY; TITANIUM; POWDER; OXIDE;

D O I：

10.1016/j.jallcom.2008.06.110

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

In order to develop a new production process for Al-Sc alloys, a fundamental study on the electrolysis in CaCl2-Sc2O3 melts was conducted using a small-scale laboratory cell. Al-Sc alloys were electrochemically produced by cathodically polarizing an Al liquid electrode in CaCl2-Sc2O3 melts at 1173 K. Metallic-colored spherical samples were produced by the electrolysis and were analyzed by XRD, EPMA, XRF, and ICP-AES. The electrolyzed samples consisted of Al and Al3Sc phases. The purity of the obtained Al-Sc alloys was greater than 99 mass%, and the calcium content was less than 0.65 mass%. This study demonstrates the feasibility of Al-Sc alloy production directly from Sc2O3 by electrochemical methods. (C) 2008 Elsevier B.V. All rights reserved.

引用

页码：124 / 130

页数：7

共 50 条

[31] Growth morphology and nucleation mechanism of primary Ll2 Al3Sc particles in Al-Sc alloys
Hyde, K.B.
Norman, A.F.
Prangnell, P.B.
Materials Science Forum, 2000, 331
[32] The growth morphology and nucleation mechanism of primary Ll2 Al3Sc particles in Al-Sc alloys
Hyde, KB
Norman, AF
Prangnell, PB
ALUMINIUM ALLOYS: THEIR PHYSICAL AND MECHANICAL PROPERTIES, PTS 1-3, 2000, 331-3 : 1013 - 1018
[33] Ultrasonic refining mechanism of ternary phase in Al-Sc based alloys prepared through molten salt electrolysis
Liu X.
Guo Z.-C.
Xue J.-L.
Wang Z.-J.
Li X.
Zhu C.-W.
Zhang P.-J.
Gongcheng Kexue Xuebao/Chinese Journal of Engineering, 2020, 42 (11): : 1465 - 1472
[34] Investigation of the electrochemical reduction of Na2Ti3O7 in CaCl2 molten salt
Liu, Kejia
Wang, Yaowu
Di, Yuezhong
Peng, Jianping
ELECTROCHIMICA ACTA, 2019, 318 : 236 - 243
[35] KF-AlF3-Sc2O3熔盐体系下沉阴极法制备Al-Sc合金的实验研究
向燕
郑鑫
张蔚
曾文华
刘红霞
张小联
稀有金属与硬质合金, 2018, 46 (02) : 37 - 41
[36] Study on the Influence of CaO on the Electrochemical Reduction of Fe2O3 in NaCl-CaCl2 Molten Salt
Li, Hui
Song, Lingyue
Liang, Jinglong
Huo, Dongxing
Cao, Weigang
Liu, Chang
MOLECULES, 2023, 28 (24):
[37] Communication-Electrodeposition of Al-Sc Alloys from LiCl-KCl Molten Salt Containing AlCl3 and ScCl3
Hirai, Tomoki
Matsushima, Hisayoshi
Ueda, Mikito
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2021, 168 (08)
[38] Electrochemical Sc2O3 single crystal growth
Imanaka, N
Kim, YW
Masui, T
Adachi, GY
CRYSTAL GROWTH & DESIGN, 2003, 3 (03) : 289 - 290
[39] Interaction between θ′-Al2Cu and Al3Sc in the heterogeneous precipitation in an Al-Cu-Sc alloy
Nakayama, Masaru
Okuyama, Tetsuya
Miura, Yasuhiro
Materials Science Forum, 2000, 331
[40] Electrochemical SC2O3 single crystal growth
Masui, T
Kim, YW
Imanaka, N
Adachi, G
JOURNAL OF ALLOYS AND COMPOUNDS, 2004, 374 (1-2) : 97 - 100

← 1 2 3 4 5 →