Fatigue life prediction for spot welds in coach-peel and lap-shear specimens with consideration of kinked crack behaviour

被引：17

作者：

Lin, SH ^{[1
]}

Pan, J ^{[1
]}

机构：

[1] Univ Michigan, Ann Arbor, MI 48109 USA

来源：

INTERNATIONAL JOURNAL OF MATERIALS & PRODUCT TECHNOLOGY | 2004年 / 20卷 / 1-3期

关键词：

spot welds; crack propagation; failure mode; fatigue life prediction;

D O I：

10.1504/IJMPT.2004.003911

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

A fracture mechanics approach is adopted to examine the fatigue lives of spot welds in coach-peel and lap-shear specimens with consideration of kinked crack behaviour. The paths of fatigue cracks near the spot welds in these two types of specimens are first discussed. A fatigue crack growth model is then developed for spot welds in these two types of specimens based on the local stress intensity factor solutions for kinked cracks and the Paris law for crack propagation. Various global stress intensity factor solutions for spot welds in these two types of specimens are used to obtain the local stress intensity factor solutions with the experimentally determined kink angles. The results indicate that the fatigue life predictions based on accurate global stress intensity factor solutions can characterize the general trend of the experimental results. The effects of the kink angle on the fatigue life predictions are also discussed.

引用

页码：31 / 50

页数：20

共 46 条

[21] Failure Mode and Fatigue Behavior of Dissimilar Laser Welds in Lap-Shear Specimens of Aluminum and Copper Sheets
Lai, Wei-Jen
Sung, Shin-Jang
Pan, Jwo
Guo, Yunan
Su, Xuming
SAE INTERNATIONAL JOURNAL OF MATERIALS AND MANUFACTURING, 2014, 7 (03) : 706 - 710
[22] Fatigue behavior of laser welds in lap-shear specimens of high strength low alloy steel sheets
Asim, Kamran
Sripichai, Kulthida
Pan, Jwo
INTERNATIONAL JOURNAL OF FATIGUE, 2014, 61 : 283 - 296
[23] Failure behaviour of laser spot welds of TRIP8oo steel sheets under coach-peel loading
Daneshpour, S.
Riekehr, S.
Kocak, M.
Ventzke, V.
Koruk, A. I.
SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2007, 12 (06) : 508 - 515
[24] Fatigue behavior of dissimilar ultrasonic welds in lap-shear specimens of AZ31 and steel sheets
Rinker, Teresa J.
Pan, Jwo
Santella, Michael
Pan, Tsung-Yu
ENGINEERING FRACTURE MECHANICS, 2018, 189 : 405 - 426
[25] Fatigue Behavior of Laser Welds in Lap-Shear Specimens of High Strength Low Alloy (HSLA) Steels
Sripichai, K.
Asim, K.
Jo, W. H.
Pan, J.
Li, M.
SAE INTERNATIONAL JOURNAL OF MATERIALS AND MANUFACTURING, 2009, 2 (01) : 40 - 46
[26] Modeling of failure near spot welds in lap-shear specimens based on a plane stress rigid inclusion analysis
Lin, P. -C.
Lin, S. -H.
Pan, J.
ENGINEERING FRACTURE MECHANICS, 2006, 73 (15) : 2229 - 2249
[27] Failure modes and fatigue life estimations of spot friction welds in lap-shear specimens of aluminum 6111-T4 sheets. Part 2: Welds made by a flat tool
Lin, P. -C.
Pan, J.
Pan, T.
INTERNATIONAL JOURNAL OF FATIGUE, 2008, 30 (01) : 90 - 105
[28] Failure modes and fatigue life estimations of spot friction welds in lap-shear specimens of aluminum 6111-T4 sheets. Part 1: Welds made by a concave tool
Lin, P. -C.
Pan, J.
Pan, T.
INTERNATIONAL JOURNAL OF FATIGUE, 2008, 30 (01) : 74 - 89
[29] Stress intensity factor solutions for similar and dissimilar spot welds in lap-shear specimens under clamped loading conditions
Sung, Shin-Jang
Chen, Jifan
Pan, Jwo
ENGINEERING FRACTURE MECHANICS, 2017, 179 : 328 - 347
[30] Microstructures and failure mechanisms of spot friction welds in lap-shear specimens of aluminum 6061-t6 sheets
Wang, Dung-An
Lee, Sheng-Chiang
Hsieh, Kang-Yuan
Manufacturing Engineering and Materials Handling, 2005 Pts A and B, 2005, 16 : 1057 - 1061

← 1 2 3 4 5 →