Preparation of monolithic titania aerogels with high surface area by a sol-gel process combined surface modification

被引：31

作者：

Yang, Hui ^{[1
]}

Zhu, Wenjun ^{[1
]}

Sun, Sai ^{[1
]}

Guo, Xingzhong ^{[1
]}

机构：

[1] Zhejiang Univ, Dept Mat Sci & Engn, Hangzhou 310003, Zhejiang, Peoples R China

来源：

RSC ADVANCES | 2014年 / 4卷 / 62期

基金：

中国国家自然科学基金;

关键词：

26;

D O I：

10.1039/c4ra03812f

中图分类号：

O6 [化学];

学科分类号：

0703 ;

摘要：

Monolithic titania (TiO2) aerogels with high surface area were successfully synthesized by the sol-gel process combined surface modification, followed by ambient pressure drying to remove the solvents from the gels. The effects of surface modification used polyethylene glycol (PEG) 2000 as surfactant on the gelation and microstructure of the aerogel were studied in detail. The resultant aerogel with the PEG 2000:TBOT (molar ratio) of 0.005 exhibits specific surface area as high as 495 m(2) g(-1), apparent density of 0.716 g cm(-3) and porosity of 81.6%. The crystallization of aerogels after heat-treatment does not spoil the monolithic shape and morphology of the aerogel basically, and the specific surface area still keeps a relatively high value of 209 m(2) g(-1). The facile route provides a low-cost strategy for the preparation of metal oxide aerogels with high surface area.

引用

页码：32934 / 32940

页数：7

共 50 条

[41] Preparation of high surface area titania (TiO2)films and powders using particulate sol-gel route aided by polymeric fugitive agents
Mohammadi, M. R.
Cordero-Cabrera, M. C.
Fray, D. J.
Ghorbani, A.
SENSORS AND ACTUATORS B-CHEMICAL, 2006, 120 (01): : 86 - 95
[42] Synthesis of high surface performance SiO2 Gel by Sol-Gel process
Jianzhu Cailiao Xuebao, 2 (155-159):
[43] MONOLITHIC GLASS VIA SOL-GEL PROCESS
CHI, FK
AMERICAN CERAMIC SOCIETY BULLETIN, 1982, 61 (11): : 1192 - 1192
[44] Synthesis of high surface area potassium hexatitanate powders by sol-gel method
Jung, KT
Shul, YG
JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY, 1996, 6 (03) : 227 - 233
[45] High surface area nickel aluminate spinels prepared by a sol-gel method
Areán, CO
Mentruit, MP
López, AJL
Parra, JB
COLLOIDS AND SURFACES A-PHYSICOCHEMICAL AND ENGINEERING ASPECTS, 2001, 180 (03) : 253 - 258
[46] Synthesis of high surface area phosphosilicate glasses by a modified sol-gel method
Aronne, A
Turco, M
Bagnasco, G
Pernice, P
Di Serio, M
Clayden, NJ
Marenna, E
Fanelli, E
CHEMISTRY OF MATERIALS, 2005, 17 (08) : 2081 - 2090
[47] Preparation of titania/silica composite microspheres by sol-gel process in reverse suspension
Kimura, I
Kase, T
Taguchi, Y
Tanaka, M
MATERIALS RESEARCH BULLETIN, 2003, 38 (04) : 585 - 597
[48] Fabrication of superhydrophobic wood surface by a sol-gel process
Wang, Shuliang
Liu, Changyu
Liu, Guochao
Zhang, Ming
Li, Jian
Wang, Chengyu
APPLIED SURFACE SCIENCE, 2011, 258 (02) : 806 - 810
[49] Synthesis and structural characteristics of high surface area TiO2 aerogels by ultrasonic-assisted sol-gel method
Feng Qingge
Cai Huidong
Lin Haiying
Qin Siying
Liu Zheng
Ma Dachao
Ye Yuyang
NANOTECHNOLOGY, 2018, 29 (07)
[50] Preparation and characterisation of titania/hydroxyapatite composite coatings obtained by sol-gel process
Milella, E
Cosentino, F
Licciulli, A
Massaro, C
BIOMATERIALS, 2001, 22 (11) : 1425 - 1431

← 1 2 3 4 5 →