Hydrogen assisted cracking of high-strength steels for civil engineering purposes

被引：0
|
作者：
Toribio, J [1 ]
Ovejero, E [1 ]
机构：
[1] Univ A Coruna, Dept Mat Sci, ETSI Caminos, La Coruna 15192, Spain
来源：
ECF 12: FRACTURE FROM DEFECTS, VOLS. I-III | 1998年
关键词：
D O I：
暂无
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Progressive cold drawing in eutectoid steels affects the material microstructure producing orientation and packing of the pearlite lamellae, as well as orientation and enlargement of the pearlite colonies. In this paper the consequences of this evolution on the hydrogen induced fracture behaviour of the steels is studied. Results show that cold drawing produces anisotropy in the steel, so that the resistance to hydrogen assisted cracking is a directional property dependent on the angle with the cold drawing direction.
引用
收藏
页码：1127 / 1132
页数：6
相关论文
共 50 条
  • [41] Function of hydrogen in embrittlement of high-strength steels
    Nagumo, M
    ISIJ INTERNATIONAL, 2001, 41 (06) : 590 - 598
  • [42] HYDROGEN IMPACT OF HIGH-STRENGTH STEELS EMBRITTLEMENT
    Bystriansky, Jaroslav
    Sefl, Vaclav
    Rapouch, Jiri
    Horsak, Lukas
    Prikasky, Martin
    Malanik, Karel
    21ST INTERNATIONAL CONFERENCE ON METALLURGY AND MATERIALS (METAL 2012), 2012, : 954 - 960
  • [43] Hydrogen Environment Assisted Cracking of Modern Ultra-High Strength Martensitic Steels
    Pioszak, Greger L.
    Gangloff, Richard P.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2017, 48A (09): : 4025 - 4045
  • [44] Hydrogen Environment Assisted Cracking of Modern Ultra-High Strength Martensitic Steels
    Greger L. Pioszak
    Richard P. Gangloff
    Metallurgical and Materials Transactions A, 2017, 48 : 4025 - 4045
  • [45] Characteristics of hydrogen embrittlement, stress corrosion cracking and tempered martensite embrittlement in high-strength steels
    Eliaz, N
    Shachar, A
    Tal, B
    Eliezer, D
    ENGINEERING FAILURE ANALYSIS, 2002, 9 (02) : 167 - 184
  • [46] HYDROGEN-ASSISTED CRACKING THRESHOLD OF HIGH-STRENGTH LOW-ALLOY STEEL
    Yanagisawa, Yusuke
    Yoru, Wada
    Ohmi, Toshihito
    Yokobori, A. Toshimitsu
    ASME PRESSURE VESSELS AND PIPING CONFERENCE - 2015, VOL 6B, 2015,
  • [47] ASSESSING HYDROGEN-ASSISTED CRACKING FRACTURE MODES IN HIGH-STRENGTH STEEL WELDMENTS
    GEDEON, SA
    EAGAR, TW
    WELDING JOURNAL, 1990, 69 (06) : S213 - S220
  • [48] HIGH-STRENGTH STEELS WITH IMPROVED SULFIDE STRESS CRACKING RESISTANCE
    CHAVANE, A
    HABASHI, M
    PRESSOUYRE, GM
    GALLAND, J
    CORROSION, 1986, 42 (01) : 54 - 61
  • [49] Effects of Cathodic Protection on Cracking of High-Strength Pipeline Steels
    Elboujdaini, M.
    Revie, R. W.
    Attard, M.
    PROCEEDINGS OF THE ASME INTERNATIONAL PIPELINE CONFERENCE 2010, VOL 1, 2010, : 683 - 697
  • [50] Corrosion cracking of high-strength stainless steels and its diagnosis
    Belous, VY
    Gurvich, LY
    Zhirnov, AD
    Kafelnikov, VV
    Lashchevskii, VB
    Rechmenskaya, AG
    Usankova, LA
    Shubadeeva, LI
    PROTECTION OF METALS, 1997, 33 (01): : 37 - 45
12345