Effect of steel microstructure on corrosion rate and protective iron carbonate film formation

被引：69
|
作者：
Dugstad, A [1 ]
Hemmer, H [1 ]
Seiersten, M [1 ]
机构：
[1] Inst Energy Technol, N-2007 Kjeller, Norway
来源：
CORROSION | 2001年 / 57卷 / 04期
关键词：
sweet corrosion; carbon steel; microstructure; protective films;
D O I：
10.5006/1.3290361
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Three low-alloy carbon steels were given different heat treatments before testing in a corrosion flow loop at 80degreesC. Both the general corrosion rate and the susceptibility to form localized attack were significantly affected by the tempering temperature and the size and distribution of the carbides. Two of the steels contained a small amount of chromium, and the presence of chromium improved the persistence of the corrosion film for all the heat-treated samples.
引用
收藏
页码：369 / 378
页数：10
相关论文
共 50 条
  • [41] Investigation of the Influence of the Steel 20 Microstructure on the Carbon Dioxide Corrosion Rate
    Yudin, P. E.
    Pugacheva, T. M.
    Kondratyeva, L. A.
    Bogatov, M. V.
    METAL SCIENCE AND HEAT TREATMENT, 2020, 62 (5-6) : 415 - 419
  • [42] The effect of Al and Nb contents, cooling rate and rolling condition on the microstructure and corrosion behaviour of HSLA steel
    Qaban, Abdullah
    Mohmed, Tasneem
    Quazi, M. M.
    Naher, Sumsun
    MATERIALS TODAY COMMUNICATIONS, 2020, 25
  • [43] Formation of a protective layer in the course of inhibition of acidic corrosion of iron by dibenzylsulfoxide
    Dorfman, AM
    Lyakhovich, AM
    Mikhailova, SS
    Pletnev, MA
    Reshetnikov, SM
    Cheremnykh, OA
    PROTECTION OF METALS, 1997, 33 (02): : 107 - 110
  • [44] Formation of a protective layer in the course of inhibition of acidic corrosion of iron by dibenzylsulfoxide
    Fiziko-Tekhnicheskij Inst UrO RAN, Ekaterinburg, Russia
    Zashch Met, 2 (128-131):
  • [45] Visual Analysis of the Protective Effect of Asphalt Coating on MOCC against Steel Corrosion and Rust Crack Formation
    Penghui Wang
    Hongxia Qiao
    Qiong Feng
    Cuizhen Xue
    KSCE Journal of Civil Engineering, 2023, 27 : 769 - 781
  • [46] Effect of Heating Rate on Microstructure and Corrosion Resistance of Quenched and Tempered 8620 Low Carbon Alloy Steel
    Tajmiri, Sina
    Haider, Waseem
    Shabib, Ishraq
    CORROSION AND MATERIALS DEGRADATION, 2024, 5 (03) : 370 - 386
  • [47] Visual Analysis of the Protective Effect of Asphalt Coating on MOCC against Steel Corrosion and Rust Crack Formation
    Wang, Penghui
    Qiao, Hongxia
    Feng, Qiong
    Xue, Cuizhen
    KSCE JOURNAL OF CIVIL ENGINEERING, 2023, 27 (02) : 769 - 781
  • [48] The effect of bicarbonate/carbonate ions on the formation of iron rust
    Music, S
    Nowik, I
    Ristic, M
    Orehovec, Z
    Popovic, S
    CROATICA CHEMICA ACTA, 2004, 77 (1-2) : 141 - 151
  • [49] Protective effect of imidazobenzimidazoline dihydrochlorides against the acid corrosion of steel
    Berezhnaya, A. G.
    Krotky, I. I.
    Chernyavina, V. V.
    INTERNATIONAL JOURNAL OF CORROSION AND SCALE INHIBITION, 2023, 12 (04): : 2418 - 2430
  • [50] Effect of an organic binder protective coating on the corrosion resistance of steel
    Yakovleva, Ariadna A.
    Antsiferov, Evgenii A.
    Guseva, Elena A.
    Sadlovsky, Sergei, V
    IZVESTIYA VUZOV-PRIKLADNAYA KHIMIYA I BIOTEKHNOLOGIYA, 2019, 9 (04): : 600 - 611
12345