Oxidation behavior of a single-crystal Ni-base superalloy in air at 900, 1000 and 1100 °C

被引：1
|
作者：
Huang, L. [1 ]
Sun, X. F. [1 ]
Guan, H. R. [1 ]
Hu, Z. Q. [1 ]
机构：
[1] Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China
来源：
TRIBOLOGY LETTERS | 2006年 / 23卷 / 01期
关键词：
Ni-base single-crystal; superalloy; oxidation; microstructure; kinetics;
D O I：
10.1007/s11249-006-9099-3
中图分类号：
TQ [化学工业];
学科分类号：
0817 ;
摘要：
The isothermal oxidation behavior of a single-crystal (SC) Ni-base superalloy was studied over the temperature range from 900 to 1100 degrees C and analyzed by OM, TGA, XRD, EDX, SEM and EPMA. The alloy obeyed subparabolic rate law during oxidation at 900 and 1000 degrees C, whereas the alloy showed parabolic rate law at 1100 degrees C exposure. The variations in the chemical composition due to segregations, which resulted from the solidification process, led to the formation of different kinds of oxide scale on the dendritic and interdendritic area during oxidation at 900 and 1000 degrees C, while the alloy exhibited relatively uniform oxidation at 1100 degrees C. The growth mechanism of the scale was discussed.
引用
收藏
页码：15 / 22
页数：8
相关论文
共 50 条
  • [41] SINGLE-CRYSTAL SOLIDIFICATION OF A NI-BASE SUPERALLOY SRR-99
    MA, DX
    SAHM, PR
    ZEITSCHRIFT FUR METALLKUNDE, 1991, 82 (11): : 869 - 873
  • [42] Oxidation behavior characteristics of an aluminized Ni-based single crystal superalloy CM186LC between 900 °C and 1100 °C in air
    Latief, Fahamsyah H.
    Kakehi, Koji
    Tashiro, Yuma
    JOURNAL OF INDUSTRIAL AND ENGINEERING CHEMISTRY, 2013, 19 (06) : 1926 - 1932
  • [43] Oxidation behavior of high Hf nickel-based superalloy in air at 900, 1000 and 1100℃
    Jiu-han Xiao
    Ying Xiong
    Li Wang
    Xiang-wei Jiang
    Dong Wang
    Kai-wen Li
    Jia-sheng Dong
    Lang-hong Lou
    International Journal of Minerals Metallurgy and Materials, 2021, 28 (12) : 1957 - 1965
  • [44] High temperature oxidation of single-crystal Ni-base superalloys
    Bouhanek, K
    Oquab, D
    Pieraggi, B
    HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 4, PTS 1 AND 2, 1997, 251-2 : 33 - 40
  • [45] Solidification behaviours of a single-crystal Ni-base superalloy under lateral constraints
    Wang, Huaming
    Tang, Yajun
    Zhang, Jinghua
    Li, Ying'ao
    Zhang, Zhiya
    Yu, Yang
    Hu, Zhuangqi
    Cailiao Kexue Jinzhan/Materials Science Progress, 1993, 7 (02):
  • [46] Nanoindentation simulation of Ni-base single-crystal superalloy with the consideration of interface effect
    Hu Xing-Jian
    Zheng Bai-Lin
    Hu Teng-Yue
    Yang Biao
    He Peng-Fei
    Yue Zhu-Feng
    ACTA PHYSICA SINICA, 2014, 63 (17)
  • [47] Fretting on the cubic face of a single-crystal Ni-base superalloy at room temperature
    Huang, X.
    Gibson, T. E.
    Zhang, M.
    Neu, R. W.
    TRIBOLOGY INTERNATIONAL, 2009, 42 (06) : 875 - 885
  • [48] ANALYSIS OF GAMMA-' SHAPE CHANGES IN A SINGLE-CRYSTAL NI-BASE SUPERALLOY
    GAYDA, J
    MACKAY, RA
    SCRIPTA METALLURGICA, 1989, 23 (11): : 1835 - 1838
  • [49] Isothermal oxidation behaviour of a Ni-base superalloy at 900 and 1 000
    Shenyang Ligong University, Shenyang, China
    Gongneng Cailiao, 4 (04025-04030):
  • [50] Isothermal oxidation behavior of the directionally solidified Ni-based superalloy DZ951 at 900, 1000 and 1100○C
    Huang, L.
    Guan, H. R.
    Sun, X. F.
    Wang, Y. L.
    INTERNATIONAL JOURNAL OF MODERN PHYSICS B, 2006, 20 (25-27): : 3587 - 3592
12345