Oxidation behavior of a single-crystal Ni-base superalloy in air at 900, 1000 and 1100 °C

被引：1
|
作者：
Huang, L. [1 ]
Sun, X. F. [1 ]
Guan, H. R. [1 ]
Hu, Z. Q. [1 ]
机构：
[1] Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China
来源：
TRIBOLOGY LETTERS | 2006年 / 23卷 / 01期
关键词：
Ni-base single-crystal; superalloy; oxidation; microstructure; kinetics;
D O I：
10.1007/s11249-006-9099-3
中图分类号：
TQ [化学工业];
学科分类号：
0817 ;
摘要：
The isothermal oxidation behavior of a single-crystal (SC) Ni-base superalloy was studied over the temperature range from 900 to 1100 degrees C and analyzed by OM, TGA, XRD, EDX, SEM and EPMA. The alloy obeyed subparabolic rate law during oxidation at 900 and 1000 degrees C, whereas the alloy showed parabolic rate law at 1100 degrees C exposure. The variations in the chemical composition due to segregations, which resulted from the solidification process, led to the formation of different kinds of oxide scale on the dendritic and interdendritic area during oxidation at 900 and 1000 degrees C, while the alloy exhibited relatively uniform oxidation at 1100 degrees C. The growth mechanism of the scale was discussed.
引用
收藏
页码：15 / 22
页数：8
相关论文
共 50 条
  • [1] Oxidation Behavior of a Single-Crystal Ni-base Superalloy in Air at 900, 1000 and 1100°C
    L. Huang
    X. F. Sun
    H. R. Guan
    Z. Q. Hu
    Oxidation of Metals, 2006, 65 : 207 - 222
  • [2] Oxidation behavior of a single-crystal Ni-base superalloy in air at 900, 1000 and 1100°C
    Huang, L.
    Sun, X. F.
    Guan, H. R.
    Hu, Z. Q.
    OXIDATION OF METALS, 2006, 65 (3-4): : 207 - 222
  • [3] Oxidation behavior of a single-crystal Ni-base superalloy in air at 900, 1000 and 1100 °C
    L. Huang
    X.F. Sun
    H.R. Guan
    Z.Q. Hu
    Tribology Letters, 2006, 23 : 15 - 22
  • [4] Oxidation behavior of a single-crystal Ni-base superalloy in air at 900, 1000 and 1100 °C
    L. Huang
    X. F. Sun
    H. R. Guan
    Z. Q. Hu
    Tribology Letters, 2007, 27 (1) : 127 - 127
  • [5] Oxidation Behavior of the Single-Crystal Ni-base Superalloy DD32 in Air at 900, 1000, and 1100°C
    L. Huang
    X. F. Sun
    H. R. Guan
    Z. Q. Hu
    Oxidation of Metals, 2006, 65 : 391 - 408
  • [6] Oxidation behavior of the single-crystal Ni-base superalloy DD32 in air at 900, 1000, and 1100°C
    Huang, L.
    Sun, X. F.
    Guan, H. R.
    Hu, Z. Q.
    OXIDATION OF METALS, 2006, 65 (5-6): : 391 - 408
  • [7] Oxidation behavior of a single-crystal Ni-base superalloy between 900 and 1000°C in air
    Liu, C. T.
    Ma, J.
    Sun, X. F.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2010, 491 (1-2) : 522 - 526
  • [8] Oxidation Behavior of a Single-Crystal Ni-Base Superalloy in Air—II: At 1000, 1100, and 1150°C
    M.H. Li
    X.F. Sun
    T. Jin
    H.R. Guan
    Z.Q. Hu
    Oxidation of Metals, 2003, 60 : 195 - 210
  • [9] Oxidation behavior of a single-crystal Ni-base superalloy in air -: II:: At 1000, 1100, and 1150°C
    Li, MH
    Sun, XF
    Jin, T
    Guan, HR
    Hu, ZQ
    OXIDATION OF METALS, 2003, 60 (1-2): : 195 - 210
  • [10] Oxidation behavior of a single-crystal Ni-base superalloy in air at 900 and 1050 °C
    Xudong Lu
    Sugui Tian
    Xingfu Yu
    Changxin Wang
    Rare Metals, 2011, 30 : 439 - 442
12345