Thermal characterization and physico-chemical properties of Fe2O3-Mn2O3/Al2O3 systems

被引：8
|
作者：
Shaheen, WM [1 ]
Hong, KS
机构：
[1] Natl Res Ctr, Dept Phys Chem, Cairo, Egypt
[2] Korea Basic Sci Inst, Dept Phys, Seoul 136701, South Korea
来源：
JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY | 2002年 / 68卷 / 01期
关键词：
characterization; doping; solid-solid interaction; thermal decomposition;
D O I：
10.1023/A:1014929904259
中图分类号：
O414.1 [热力学];
学科分类号：
摘要：
The effect of ferric and manganese oxides dopants on thermal and physicochemical properties of Mn-oxide/Al2O3 and Fe2O3/Al2O3 systems has been studied separately. The pure and doped mixed solids were thermally treated at 400-1000degreesC. Pyrolysis of pure and doped mixed solids was investigated via thermal analysis (TG-DTG) techniques. The thermal products were characterized using XRD-analysis. The results revealed that pure ferric nitrate decomposes into Fe2O3 at 350degreesC and shows thermal stability up to 1000degreesC. Crystalline Fe3O4 and Mn3O4 phases were detected for some doped solids precalcined at 1000degreesC. Crystalline gamma-Al2O3 phase was detected for all solids preheated up to 800degreesC. Ferric and manganese oxides enhanced the formation of alpha-Al2O3 phase at 1000degreesC. Crystalline MnAl2O4 and MnFe2O4 phases were formed at 1000degreesC as a result of solid-solid interaction processes. The catalytic behavior of the thermal products was tested using the decomposition of H2O2 reaction.
引用
收藏
页码：289 / 306
页数：18
相关论文
共 50 条
  • [31] REACTIONS OF ADSORBED HYDROGEN WITH OXYGEN ON FE/AL2O3, NI/AL2O3 AND FE-NI/AL2O3 CATALYSTS
    LESNIEWSKA, E
    RYNKOWSKI, J
    PARYJCZAK, T
    PRZEMYSL CHEMICZNY, 1995, 74 (01): : 21 - 22
  • [32] The System BaO – Al2O3 – Fe2O3
    G. N. Shabanova
    S. N. Bykanov
    Refractories and Industrial Ceramics, 2002, 43 : 247 - 250
  • [33] Microwave reflection characteristics of the Fe/Al2O3 and Fe3Al/Al2O3 composites
    Wei, Jianqiang
    Wang, Jianbo
    Qiao, Liang
    Wang, Tao
    Li, Fashen
    MATERIALS SCIENCE AND ENGINEERING APPLICATIONS, PTS 1-3, 2011, 160-162 : 984 - 989
  • [34] THE EFFECTS OF CR2O3 AND FE2O3 ADDITIONS ON THE THERMAL-CONDUCTIVITY OF AL2O3
    WILLIAMS, RK
    GRAVES, RS
    JANNEY, MA
    TIEGS, TN
    YARBROUGH, DW
    JOURNAL OF APPLIED PHYSICS, 1987, 61 (10) : 4894 - 4901
  • [35] Wettability of silicon carbide ceramic by Al2O3/Dy2O3 and Al2O3/Yb2O3 systems
    J.A.da Silva
    B.M.Moreschi
    G.C.R.Garcia
    S.Ribeiro
    JournalofRareEarths, 2013, 31 (06) : 634 - 638
  • [36] Wettability of silicon carbide ceramic by Al2O3/Dy2O3 and Al2O3/Yb2O3 systems
    da Silva, J. A.
    Moreschi, B. M.
    Garcia, G. C. R.
    Ribeiro, S.
    JOURNAL OF RARE EARTHS, 2013, 31 (06) : 634 - 638
  • [37] Accommodation of impurities in α-Al2O3, α-Cr2O3 and α-Fe2O3
    Atkinson, KJW
    Grimes, RW
    Levy, MR
    Coull, ZL
    English, T
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2003, 23 (16) : 3059 - 3070
  • [38] On the absorption of ammoniac by Al2O3, Fe2O3 and Cr2O3
    Nikitin, N
    ZEITSCHRIFT FUR ANORGANISCHE UND ALLGEMEINE CHEMIE, 1926, 155 (04): : 358 - 360
  • [39] Influence of Al2O3 Content and Cooling Rate on Crystallization in Fe2O3–CaO–SiO2–Al2O3 Systems
    Tae Jun Park
    Joon Sung Choi
    Dong Joon Min
    Metals and Materials International, 2022, 28 : 2033 - 2041
  • [40] Mn改性Fe2O3/?-Al2O3脱除气相As2O3实验研究
    刘翔
    张月
    邢佳颖
    郭雨生
    许桐
    王春波
    中国电机工程学报, 2021, 41 (15) : 5250 - 5258
12345