Surface finishing: Impact on tribological characteristics of WC-Co hardmetals

被引：23
|
作者：
Bonny, K. [1 ]
De Baets, P. [1 ]
Quintelier, J. [1 ]
Vleugels, J. [2 ]
Jiang, D. [2 ]
Van der Biest, O. [2 ]
Lauwers, B. [3 ]
Liu, W. [3 ]
机构：
[1] Univ Ghent, Mech Construct & Prod Dept, BE-9000 Ghent, Belgium
[2] Catholic Univ Louvain, KU Leuven, Dept Met & Mat Engn, BE-3001 Louvain, Belgium
[3] Catholic Univ Louvain, KU Leuven, Dept Mech Engn, BE-3001 Louvain, Belgium
来源：
TRIBOLOGY INTERNATIONAL | 2010年 / 43卷 / 1-2期
关键词：
WC-Co cemented carbide; Surface finish; Wire-EDM; Dry reciprocating sliding; Pin-on-plate; RECIPROCATING SLIDING FRICTION; ELECTRICAL-DISCHARGE ENERGY; CEMENTED CARBIDES; WEAR RESPONSE; TUNGSTEN CARBIDE; ROUGHNESS; CONTACT; EDM; PARTICLES; FRACTURE;
D O I：
10.1016/j.triboint.2009.04.029
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Flat samples of WC-Co hardmetals with 6-12 wt%Co were surface finished by grinding polishing and wire-electro-discharge machining (EDM). Comparative dry reciprocating sliding experiments against WC-6wt%Co pins were performed using a Plint TE77 tribometer. Tribological characteristics were recorded online. Wear Surfaces were characterized by surface scanning topography and scanning electron microscopy. Wire-EDM'ed samples exhibited higher friction and wear compared to ground and polished equivalents. This trend was correlated to X-ray diffraction measurements revealing tensile residual surface stresses in WC after wire-EDM contrary to compressive surface stresses after grinding and polishing. However, finer executed EDM reduces friction and wear significantly. (C) 2009 Elsevier Ltd. All rights reserved.
引用
收藏
页码：40 / 54
页数：15
相关论文
共 50 条
  • [1] Nanoindentation of WC-Co hardmetals
    Duszova, Annamaria
    Halgas, Radoslav
    Bl'anda, Marek
    Hvizdos, Pavol
    Lofaj, Frantisek
    Dusza, Jan
    Morgiel, Jerzy
    [J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2013, 33 (12) : 2227 - 2232
  • [2] Grinding of WC-Co hardmetals
    Hegeman, JBJW
    De Hosson, JTM
    de With, G
    [J]. WEAR, 2001, 248 (1-2) : 187 - 196
  • [3] FRACTURE TOPOGRAPHY OF WC-CO HARDMETALS
    LEA, C
    ROEBUCK, B
    [J]. METAL SCIENCE, 1981, 15 (06): : 262 - 266
  • [4] Ultrasonic evaluation of WC-Co hardmetals
    State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan 430070, China
    [J]. Wuhan Ligong Daxue Xuebao, 2007, 10 (153-157):
  • [5] Reactive Sintering of Bimodal WC-Co Hardmetals
    Tarraste, Marek
    Juhani, Kristjan
    Pirso, Jueri
    Viljus, Mart
    [J]. MATERIALS SCIENCE-MEDZIAGOTYRA, 2015, 21 (03): : 382 - 385
  • [6] Selection of processing route for controlling the toughness characteristics of Wc-Co hardmetals
    Rengarajan, R
    Rao, SR
    Bhattacharya, P
    Prashanth, BK
    [J]. EURO PM 2002: HARD MATERIALS PROCEEDINGS, 2002, : 106 - 113
  • [7] Gradient WC-Co hardmetals: Theory and practice
    Konyashin, I.
    Ries, B.
    Lachmann, F.
    Fry, A. T.
    [J]. INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2013, 36 : 10 - 21
  • [8] Additive manufacturing of WC-Co hardmetals: a review
    Yankun Yang
    Chaoqun Zhang
    Dayong Wang
    Liping Nie
    Daniel Wellmann
    Yingtao Tian
    [J]. The International Journal of Advanced Manufacturing Technology, 2020, 108 : 1653 - 1673
  • [9] Thermally induced surface integrity changes of ground WC-Co hardmetals
    Yang, J.
    Roa, J. J.
    Schwind, M.
    Oden, M.
    Johansson-Joesaar, M. P.
    Esteve, J.
    Llanes, L.
    [J]. 3RD CIRP CONFERENCE ON SURFACE INTEGRITY, 2016, 45 : 91 - 94
  • [10] Additive manufacturing of WC-Co hardmetals: a review
    Yang, Yankun
    Zhang, Chaoqun
    Wang, Dayong
    Nie, Liping
    Wellmann, Daniel
    Tian, Yingtao
    [J]. INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2020, 108 (5-6): : 1653 - 1673