Fatigue of steam turbine blades with damage on the leading edge

被引：16
|
作者：
Shlyannikov, V. N. [1 ]
Yarullin, R. R. [1 ]
Zakharov, A. P. [1 ]
机构：
[1] Russian Acad Sci, Res Ctr Power Engn Problems, Lobachevsky St 2-31,Post Box 190, Kazan 420111, Russia
来源：
20TH EUROPEAN CONFERENCE ON FRACTURE | 2014年 / 3卷
基金：
俄罗斯基础研究基金会;
关键词：
elastic-plastic stress analysis; low-cycle fatigue test; mechanical properties; fatigue life; turbine blades; single edge notched round specimen; protective coating;
D O I：
10.1016/j.mspro.2014.06.289
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
This study is concerned with the assessment of the fatigue life of cracked steam turbine blades which operate under cyclic loading conditions. The turbine blades fatigue life estimation approach includes numerical stress-strain analysis of real rotor components, experimental study of fatigue and fracture resistance material properties and determination of crack growth rate characteristics on the round bar specimens with the single edge notch. Static and cyclic tests were performed to obtain the main mechanical properties and the fatigue life characteristics of blade's material after loading history. Both specimens with the initial surface state and specimens with high velocity air fuel (HVAF) coating were tested. As a result the fatigue life characteristics of blade's material were determined as a function of operating time. The fatigue crack growth study of surface flow was performed for round bar specimens with different initial single edge notch depth. Experimental constants describing the linear parts of the fatigue fracture diagrams were determined. (C) 2014 Published by Elsevier Ltd. Open access under CC BY license.
引用
收藏
页码：1792 / 1797
页数：6
相关论文
共 50 条
  • [1] Conditions leading to corrosion damage of steam turbine blades during turbine shutdowns
    Pomenic, L
    PROCEEDINGS OF THE 6TH INTERNATIONAL DESIGN CONFERENCE: DESIGN 2000, 2000, : 141 - 146
  • [2] Foreign object damage on the leading edge of gas turbine blades
    Marandi, Seyed Masoud
    Rahmani, Kh.
    Tajdari, Mehdi
    AEROSPACE SCIENCE AND TECHNOLOGY, 2014, 33 (01) : 65 - 75
  • [3] Fatigue damage mechanics approach to predict the end of incubation and breakthrough of leading edge protection coatings for wind turbine blades
    Tempelis, Antonios
    Jespersen, Kristine Munk
    Mishnaevsky, Leon
    International Journal of Fatigue, 2025, 190
  • [4] Erosion-fatigue of steam turbine blades
    Azevedo, C. R. F.
    Sinatora, A.
    ENGINEERING FAILURE ANALYSIS, 2009, 16 (07) : 2290 - 2303
  • [5] Corrosion-Fatigue in Steam Turbine Blades
    Salzman, R. N.
    Rieger, N. F.
    Tschegg, S.
    Schoenbauer, B.
    Turnbull, A.
    Zhou, S.
    Gandy, D.
    ADVANCES IN MATERIALS TECHNOLOGY FOR FOSSIL POWER PLANTS: PROCEEDINGS FROM THE SIXTH INTERNATIONAL CONFERENCE, 2010, 2011, : 450 - 469
  • [6] Fatigue of steam turbine blades at resonance conditions
    Rodriguez, J. A.
    Castro, L.
    Tejeda, A. L.
    Garcia, J. C.
    Rodriguez, J. M.
    Galindo, E.
    El Hamzaoui, Y.
    ENGINEERING FAILURE ANALYSIS, 2019, 104 : 39 - 46
  • [7] Detection of damage in steam turbine blades caused by low cycle and strain cycling fatigue
    Cano, S.
    Rodriguez, J. A.
    Rodriguez, J. M.
    Garcia, J. C.
    Sierra, F. Z.
    Casolco, S. R.
    Herrera, M.
    ENGINEERING FAILURE ANALYSIS, 2019, 97 : 579 - 588
  • [8] Repair and reinforcement of the leading edge of wind turbine blades
    Masek, Roman
    OCHRONA PRZED KOROZJA, 2023, 66 (04): : 122 - 123
  • [9] Fatigue lifetime prediction model for leading edge protection coating systems of wind turbine blades
    Hoksbergen, T. H.
    Akkerman, R.
    Baran, I.
    TRIBOLOGY INTERNATIONAL, 2023, 189
  • [10] Improvement of corrosion fatigue limit of steam turbine blades
    Thauvin, G
    Vittemant, B
    REVUE DE METALLURGIE-CAHIERS D INFORMATIONS TECHNIQUES, 1996, 93 (05): : 673 - &