Hydrogen effect on the field dependence of Young's modulus of FeCuNbSiB alloy

被引：9
|
作者：
Kolat, VS [1 ]
Bayri, N [1 ]
Atalay, S [1 ]
机构：
[1] Inonu Univ, Dept Phys, Sci & Arts Fac, TR-44069 Malatya, Turkey
来源：
JOURNAL OF ALLOYS AND COMPOUNDS | 2002年 / 343卷 / 1-2期
关键词：
transition metal compounds; amorphous materials; gas-solid reaction; magnetization measurements;
D O I：
10.1016/S0925-8388(02)00401-2
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
The magnitude of the magnetic field dependence of Young's modulus of FeCuNbSiB alloys was found to decrease after hydrogenation but to nearly recover after 2-3 h. A large variation in the magnetic and the magnetoelastic properties of as-received sample was observed after hydrogenation. DeltaE and M-H results of samples annealed at 450degreesC showed that annealing could reduce hydrogen permeation into the sample. Practically no variation in the magnetic and magnetoelastic properties of samples annealed at 550degreesC were observed before and after hydrogenation. (C) 2002 Elsevier Science B.V. All rights reserved.
引用
收藏
页码：234 / 237
页数：4
相关论文
共 50 条
  • [31] Size dependence of effective Young's modulus of nanoporous gold
    Mathur, Anant
    Erlebacher, Jonah
    APPLIED PHYSICS LETTERS, 2007, 90 (06)
  • [32] Thickness Dependence of the Young's Modulus of Polymer Thin Films
    Chang, Jooyoung
    Toga, Kamil B.
    Paulsen, Joseph D.
    Menon, Narayanan
    Russell, Thomas P.
    MACROMOLECULES, 2018, 51 (17) : 6764 - 6770
  • [33] Measurement of Magnetic Field dependent Young's modulus of Iron-Gallium Alloy in Flexural Mode
    Datta, Supratik
    Flatau, Alison B.
    SMART STRUCTURES AND MATERIALS 2006: ACTIVE MATERIALS: BEHAVIOR AND MECHANICS, 2006, 6170
  • [34] Poling Field Dependence of Longitudinal and Transverse Wave Velocities, Young's Modulus, and Poisson's Ratio in Piezoelectric Ceramics
    Ogawa, Toshio
    Ishii, Keisuke
    Matsumoto, Tsubasa
    Nishina, Takayuki
    JAPANESE JOURNAL OF APPLIED PHYSICS, 2012, 51 (09)
  • [35] EFFECT OF TEMPERATURE ON YOUNG'S MODULUS OF GRAPHENE
    Mirnezhad, M.
    Modarresi, M.
    Ansari, R.
    Roknabadi, M. R.
    JOURNAL OF THERMAL STRESSES, 2012, 35 (10) : 913 - 920
  • [36] Effect of TiB2 on damping capacity and dynamic Young's modulus of 2219 alloy
    Chen, Dong
    Zhou, Cong
    Li, Xianfeng
    Zhang, Yijie
    Ma, Naiheng
    MECHANICAL ENGINEERING, MATERIALS SCIENCE AND CIVIL ENGINEERING II, 2014, 470 : 27 - 30
  • [37] Effect of swaging on Young's modulus of β Ti-33.6Nb-4Sn alloy
    Hanada, Shuji
    Masahashi, Naoya
    Jung, Taek Kyun
    Miyake, Masahiro
    Sato, Yutaka S.
    Kokawa, Hiroyuki
    JOURNAL OF THE MECHANICAL BEHAVIOR OF BIOMEDICAL MATERIALS, 2014, 32 : 310 - 320
  • [38] Effect of porosity on Young's modulus of a porcelain
    Pickup, R
    BRITISH CERAMIC TRANSACTIONS, 1997, 96 (03): : 96 - 98
  • [39] The effect of YSZ microstructure on Young's modulus
    Michlik, P
    Racek, O
    Berndt, CC
    THERMAL SPRAY 2004: ADVANCES IN TECHNOLOGY AND APPLICATION, PROCEEDINGS, 2004, : 1110 - 1118
  • [40] Effect of compositional modification on Young's modulus of Ti2AlNb-based alloy
    Tang, F
    Awane, T
    Hagiwara, M
    SCRIPTA MATERIALIA, 2002, 46 (02) : 143 - 147
12345