Investigation of influence of micro-structure on magnetic properties of amorphous powder core

被引：0
|
作者：
Guo Feng [1 ]
Ba Shan
Li Deren
Lu Zhichao
Lu Caowei
Wang Jun
机构：
[1] Adv Technol & Mat Co Ltd, Cent Iron & Steel Res Inst, Beijing 100081, Peoples R China
[2] Beijing Inst Technol, Sch Sci, Beijing 100081, Peoples R China
来源：
RARE METALS | 2006年 / 25卷
关键词：
amorphous powder core; core loss; permeability; DC-bias characteristic; annealing;
D O I：
10.1016/S1001-0521(07)60125-9
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The influence of micro-structure on magnetic properties of amorphous powder core was investigated. The results show that the amorphous powders of the powder core become crystallized with the increase of annealing temperature, and the permeability decreases from 60 to 12, the core loss increases from 0.2 to 0.3 W center dot cm(-3), DC-bias characteristic was improved with further increase of annealing temperature, and the magnetic properties become deteriorated due to decrease of permeability and enhancement of coercive force resulting from the crystallization of amorphous powder.