Phase Equilibria in the CaO-SiO2-Al2O3-MgO System with CaO/SiO2 Ratio of 1.3 Relevant to Iron Blast Furnace Slags

被引：32
|
作者：
Ma, Xiaodong [1 ]
Wang, Geoff [1 ]
Wu, Shengli [2 ]
Zhu, Jinming [2 ]
Zha, Baojun [1 ]
机构：
[1] Univ Queensland, Sch Chem Engn, Brisbane, Qld 4072, Australia
[2] Baoshan Iron & Steel Baosteel Co Ltd, Shanghai 201900, Peoples R China
来源：
ISIJ INTERNATIONAL | 2015年 / 55卷 / 11期
关键词：
liquidus temperature; CaO-SiO2-Al2O3-MgO system; BF slag; EPMA; MELTING BEHAVIOR; SINTER; AL2O3; ORE;
D O I：
10.2355/isijinternational.ISIJINT-2015-263
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Phase equilibria and liquidus temperatures in the CaO-SiO2-Al2O3-MgO system with CaO/SiO2 weight ratio of 1.30 have been experimentally determined by means of high temperature equilibration and quenching technique followed by electron probe X-ray microanalysis. Isotherms between 1 723 and 1 773 K were determined in the primary phase fields of melilite, dicalcium silicate, spinel, merwinite and periclase that are relevant to ironmaking slags. Effects of Al2O3, MgO and CaO/SiO2 ratio on the liquidus temperatures have been discussed. Compositions of the solid phases corresponding to the liquidus have been accurately measured that will be used for development of the thermodynamic database.
引用
收藏
页码：2310 / 2317
页数：8
相关论文
共 50 条
  • [1] Phase Equilibria in the System "FeO"-CaO-SiO2-Al2O3-MgO with CaO/SiO2 1.3
    Jang, Kyoung-oh
    Ma, Xiaodong
    Zhu, Jinming
    Xu, Haifa
    Wang, Geoff
    Zhao, Baojun
    [J]. ISIJ INTERNATIONAL, 2016, 56 (06) : 967 - 976
  • [2] Phase Equilibria Studies in the CaO-SiO2-Al2O3-MgO System with CaO/SiO2 Ratio of 1.10
    Ma, Xiaodong
    Zhang, Dianwei
    Zhao, Zhixing
    Evans, Tim
    Zhao, Baojun
    [J]. ISIJ INTERNATIONAL, 2016, 56 (04) : 513 - 519
  • [3] Phase Equilibria in the System “FeO”-CaO-SiO2-Al2O3-MgO at Different CaO/SiO2 Ratios
    Kyoung-oh Jang
    Xiaodong Ma
    Jinming Zhu
    Haifa Xu
    Geoff Wang
    Baojun Zhao
    [J]. Metallurgical and Materials Transactions B, 2017, 48 : 1547 - 1560
  • [4] Phase Equilibria in the System "FeO"-CaO-SiO2-Al2O3-MgO at Different CaO/SiO2 Ratios
    Jang, Kyoung-oh
    Ma, Xiaodong
    Zhu, Jinming
    Xu, Haifa
    Wang, Geoff
    Zhao, Baojun
    [J]. METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2017, 48 (03): : 1547 - 1560
  • [5] Phase equilibria studies in the CaO-SiO2-Al2O3-MgO system with CaO/SiO2ratio of 0.9
    Wang, Dongqing
    Chen, Mao
    Jiang, Yang
    Wang, Shuai
    Zhao, Zhixing
    Evans, Tim
    Zhao, Baojun
    [J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2020, 103 (12) : 7299 - 7309
  • [6] Activity of CaO in CaO-SiO2-Al2O3-MgO Slags
    Wen, Qiulin
    Shen, Fengman
    Zheng, Haiyan
    Yu, Jiyang
    Jiang, Xin
    Gao, Qiangjian
    [J]. ISIJ INTERNATIONAL, 2018, 58 (05) : 792 - 798
  • [7] Phase Equilibria in the System CaO-SiO2-Al2O3-MgO-15 and 20 wt% "FeO" with CaO/SiO2 Ratio of 1.3
    Jang, Kyoung-oh
    Ma, Xiaodong
    Zhu, Jinming
    Xu, Haifa
    Wang, Geoff
    Zhao, Baojun
    [J]. ISIJ INTERNATIONAL, 2016, 56 (10) : 1728 - 1737
  • [8] Effect of CaO/SiO2 Ratio on Surface Tension of CaO-SiO2-Al2O3-MgO Melts
    Sukenaga, Sohei
    Higo, Tomoyuki
    Shibata, Hiroyuki
    Saito, Noritaka
    Nakashima, Kunihiko
    [J]. ISIJ INTERNATIONAL, 2015, 55 (06) : 1299 - 1304
  • [9] Phase Equilibrium Studies in the CaO-SiO2-Al2O3-MgO System with MgO/CaO Ratio of 0.2
    Liao, Jinfa
    Qing, Gele
    Zhao, Baojun
    [J]. METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2023, 54 (02): : 793 - 806
  • [10] CRYSTALLIZATION KINETICS OF CaO-SiO2-Al2O3-MgO SLAGS
    Esfahani, Shaghayegh
    Barati, Mansoor
    [J]. ADVANCES IN MOLTEN SLAGS, FLUXES, AND SALTS, 2016, : 237 - 244
12345