Modeling board-level four-point bend fatigue and impact drop tests

被引：9

作者：

Che, F. X. ^{[1
]}

Pang, John H. L. ^{[1
]}

机构：

[1] Nanyang Technol Univ, Sch Mech & Aerosp Engn, 50 Nanyang Ave, Singapore 639798, Singapore

来源：

56TH ELECTRONIC COMPONENTS & TECHNOLOGY CONFERENCE 2006, VOL 1 AND 2, PROCEEDINGS | 2006年

关键词：

D O I：

10.1109/ECTC.2006.1645684

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In this paper modeling and simulation of board-level four-point bend fatigue and impact tests were investigated for 7mm x 7mm VQFN(48I/O) assembly and 15mm x 15mm FBGA(324I/O) assembly with Sn-Ag-Cu lead-free solder and OSP board surface finish. For cyclic bending fatigue, four-point bend cyclic loading at room temperature (25 degrees C) and at high temperature (125 degrees C) were investigated in order to develop bend fatigue model for Pb-free solder. The acceleration factor of failure at high temperature (125 degrees C) to room temperature (25 degrees C) will be presented. Test results show that the cycle to failure increases significantly when bending displacement ranges decrease for both bend tests at 25 degrees C an 125 degrees C. The acceleration factor of cycle to failure due to high temperature (125 degrees C) effect is higher than that due to room temperature effect. The FBGA component has higher bending fatigue resistance compared to VQFN component. Accumulated energy density per cycle at 125 degrees C is more than that at 25 degrees C significantly, which indicates that higher temperature accelerates bending fatigue failure of solder. Energy-based bending fatigue models were developed for Sn-Ag-Cu. lead free solder subjected to cyclic bending load at 25 degrees C and 125 degrees C based on FEA result and experimental data. Using the same FEA model the loading was changed to simulate a four-point bend impact test with the same corresponding magnitude of bending curvatures. Comparisons of solder joint deformation response between the slow cyclic bend test and impact drop bend test will be presented.

引用

页码：443 / +

页数：2

共 50 条

[11] Investigation into the size effect on four-point bending fatigue tests
Li, N.
Molenaar, A. A. A.
van de Ven, M. F. C.
Pronk, A. C.
Wu, S.
FOUR-POINT BENDING, 2012, : 35 - 47
[12] Evaluating four-point bend fatigue of asphalt mix using image analysis
Hartman, AM
Gilchrist, MC
JOURNAL OF MATERIALS IN CIVIL ENGINEERING, 2004, 16 (01) : 60 - 68
[13] Dynamic stress of solder joints under board-level Drop/Impact
Bai, Jie
Qin, Fei
An, Tong
ICEPT: 2007 8TH INTERNATIONAL CONFERENCE ON ELECTRONICS PACKAGING TECHNOLOGY, PROCEEDINGS, 2007, : 187 - +
[14] Novel stress analysis method on board-level during drop tests for electrical components
Huotari, J.
Inkeri, T.
MICROELECTRONICS RELIABILITY, 2022, 138
[15] Novel stress analysis method on board-level during drop tests for electrical components
Huotari, J.
Inkeri, T.
Microelectronics Reliability, 2022, 138
[16] Evolution of the Modulus of Asphalt Concrete in Four-Point Beam Fatigue Tests
Abhijith, B. S.
Narayan, S. P. Atul
JOURNAL OF MATERIALS IN CIVIL ENGINEERING, 2020, 32 (10)
[17] An approach to adjust the board-level drop test conditions to improve the correlation with product-level drop impact
Mattila, T. T.
Ruotoistenmaki, H.
Raami, J.
Hokka, J.
Makela, M.
Hussa, E.
Sillanpaa, M.
Halkola, V.
MICROELECTRONICS RELIABILITY, 2014, 54 (04) : 785 - 795
[18] Comparison of Uniaxial and Four-Point Bending Fatigue Tests for Asphalt Mixtures
Li, Ning
Pronk, A. C.
Molenaar, A. A. A.
van de Ven, M. F. C.
Wu, Shaopeng
TRANSPORTATION RESEARCH RECORD, 2013, (2373) : 44 - 53
[19] Dynamic response of a board-level electronic package under drop impact load
State Key Laboratory of Mechanical System and Vibration, School of Mechanical Engineering, Shanghai Jiaotong University, Shanghai 200240, China
J Vib Shock, 2008, 6 (108-113):
[20] Influence of bending rotations on three and four-point bend end notched flexure tests
Arrese, A.
Mujika, F.
ENGINEERING FRACTURE MECHANICS, 2008, 75 (14) : 4234 - 4246

← 1 2 3 4 5 →