Preparation of carbon coated LiFePO4 by a combination of spray pyrolysis with planetary ball-milling followed by heat treatment and their electrochemical properties

被引：91

作者：

Konarova, Muxina ^{[1
]}

Taniguchi, Izumi ^{[1
]}

机构：

[1] Tokyo Inst Technol, Dept Chem Engn, Grad Sch Sci & Engn, Meguro Ku, Tokyo 1528552, Japan

来源：

POWDER TECHNOLOGY | 2009年 / 191卷 / 1-2期

关键词：

Carbon coating; LiFePO4; Ball milling; Spray pyrolysis; Lithium-ion batteries; Cathode; PHOSPHO-OLIVINES; CATHODE MATERIAL; PERFORMANCE; POWDERS; CONDUCTIVITY; TEMPERATURE; GRAPHITE; BLACK; FE2P;

D O I：

10.1016/j.powtec.2008.09.013

中图分类号：

TQ [化学工业];

学科分类号：

0817 ;

摘要：

Carbon coated LiFePO4 could be successfully prepared by a combination of spray pyrolysis (SP) with planetary ball-milling (BM) followed by heat treatment at 500 degrees C. SEM and TEM observations revealed that the carbon coated LiFePO4 were much smaller in size than the bare LiFePO4 prepared by the SP followed by heat treatment at 600 degrees C and the ball-milled bare LiFePO4 prepared by the combination of SP with BM followed by heat treatment at 500 degrees C. Furthermore, TEM observations also suggested that conductive carbon could be distributed well on the surface of LiFePO4. The electrochemical measurements demonstrated that the carbon coated LiFePO4 Could deliver better battery performance in terms of the discharge capacity, cycling stability and rate capability than the bare LiFePO4 and the ball-milled bare LiFePO4. It exhibited first-discharge capacities of 158 mAh g(-1) at 0.1C and 114 mAh g-1 at 5C with excellent cycle performances at 25 degrees C The cell. tested at 60 degrees C delivered the theoretical capacity (170 mAh g(-1)) at 0.1C and 78% (133 mAh g(-1)) of theoretical capacity at 5C, respectively. (C) 2008 Elsevier B.V. All rights reserved.