Stress corrosion cracking of API X-60 pipeline in a soil containing water

被引：21
|
作者：
Pan, B. W.
Peng, X.
Chu, W. Y. [1 ]
Su, Y. J.
Qiao, L. J.
机构：
[1] Univ Sci & Technol Beijing, Dept Mat Phys, Beijing 100083, Peoples R China
[2] N Univ China, Minist Educ, Key Lab Instrumentat Sci & Dynam Measurement, Taiyuan 030051, Peoples R China
来源：
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2006年 / 434卷 / 1-2期
基金：
中国国家自然科学基金;
关键词：
API X-60 pipeline; soil containing water; stress corrosion cracking; corrosion-induced stress;
D O I：
10.1016/j.msea.2006.06.087
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Stress corrosion cracking (SCC) of a API X-60 pipeline steel in a soil containing 33% water has been investigated using slow strain rate tests and sustained load test of single-edge cracked sample. The results showed that a transgranular SCC in the soil occurred when epsilon < 3.5 x 10(-7) s(-1), and the susceptibility to SCC was about 30%. SCC of the cracked sample in the soil at sustained load could also occur, and the threshold stress intensity factor of SCC was K-ISCC= 0.73K(C). (c) 2006 Elsevier B.V. All rights reserved.
引用
收藏
页码：76 / 81
页数：6
相关论文
共 50 条
  • [1] Role of Hydrogen in Stress Corrosion Cracking of X-60 Pipeline Steel in Soil Containing Water
    Pan, B. W.
    Li, J. X.
    Su, Y. J.
    Chu, W. Y.
    Qiao, L. J.
    CORROSION, 2012, 68 (11) : 1029 - 1036
  • [2] Transgranular stress corrosion cracking of X-60 pipeline steel in simulated ground water
    Zhang, XY
    Lambert, SB
    Sutherby, R
    Plumtree, A
    CORROSION, 1999, 55 (03) : 297 - 305
  • [3] Stress corrosion cracking of X60 pipeline in soil
    Key Laboratory of Instrumentation Science and Dynamic Measurement, North University of China, Taiyuan 030051, China
    不详
    Zhongbei Daxue Xuebao (Ziran Kexue Ban), 2007, 3 (267-271):
  • [4] Sulfide stress cracking susceptibility of welded X-60 and X-65 pipeline steels
    Natividad, C.
    Salazar, M.
    Contreras, A.
    Albiter, A.
    Perez, R.
    Gonzalez-Rodriguez, J. G.
    CORROSION, 2006, 62 (05) : 375 - 382
  • [5] Stress Corrosion Cracking of Welded API X70 Pipeline Steel in Simulated Underground Water
    Z. Y. Liu
    C. W. Du
    C. Li
    F. M. Wang
    X. G. Li
    Journal of Materials Engineering and Performance, 2013, 22 : 2550 - 2556
  • [6] Stress Corrosion Cracking of Welded API X70 Pipeline Steel in Simulated Underground Water
    Liu, Z. Y.
    Du, C. W.
    Li, C.
    Wang, F. M.
    Li, X. G.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2013, 22 (09) : 2550 - 2556
  • [7] Corrosion behavior of API 5L X-60 pipeline steel exposed to near-neutral pH soil simulating solution
    Benmoussa, A.
    Hadjel, M.
    Traisnel, M.
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2006, 57 (10): : 771 - 777
  • [8] STRESS-CORROSION CRACKING OF X-60 LINE PIPE STEEL IN A CARBONATE-BICARBONATE SOLUTION
    PILKEY, AK
    LAMBERT, SB
    PLUMTREE, A
    CORROSION, 1995, 51 (02) : 91 - 96
  • [9] Effect of non-conventional heat treatment of API X60 pipeline steel on corrosion resistance and stress corrosion cracking susceptibility
    Ricardo Jacobo, Luis
    Garcia, Rafael
    Hugo Lopez, Victor
    Contreras, Antonio
    ANTI-CORROSION METHODS AND MATERIALS, 2019, 66 (03) : 274 - 285
  • [10] Stress Corrosion Cracking of X70 Pipeline Steel immersed in Synthetic Soil solution
    Galvan-Martinez, R.
    Carmona, A.
    Baltazar, M.
    Contreras, A.
    Orozco-Cruz, R.
    AFINIDAD, 2019, 76 (585) : 52 - 62
12345