Effect of curing temperature and relative humidity on the hydrates and porosity of calcium sulfoaluminate cement

被引：54
|
作者：
Li, Lin [1 ]
Wang, Ru [1 ,2 ]
Zhang, Shaokang [1 ]
机构：
[1] Tongji Univ, Sch Mat Sci & Engn, Shanghai 201804, Peoples R China
[2] Tongji Univ, Minist Educ, Key Lab Adv Civil Engn Mat, Shanghai 201804, Peoples R China
来源：
CONSTRUCTION AND BUILDING MATERIALS | 2019年 / 213卷
基金：
中国国家自然科学基金;
关键词：
Calcium sulfoaluminate cement; Curing conditions; Hydrates; Porosity; STABILITY; WATER; SULFATE; GYPSUM; ETTRINGITE; ANHYDRITE; KINETICS; IMPACT; PHASE;
D O I：
10.1016/j.conbuildmat.2019.04.044
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
The main objective of this study was to investigate the effect of curing temperature and relatively humidity (RH) on the hydrates and porosity of calcium sulfoaluminate (CSA) cement pastes. A series of experiments including X-ray diffraction (XRD), thermogravimetric (TG) and mercury intrusion porosimetry (MIP) were performed. The results indicate that the formation of hydration products and pore characteristics of CSA cement are dependent on the curing conditions. The formation of ettringite is favor of curing with low temperature and high RH. The rate of formation of aluminum hydroxide (AH(3)) and monosulfoaluminate (Ms) is well promoted when curing temperature and RH are rising. The total porosity of CSA cement paste is gradually decreased by curing with low temperature and high RH. (C) 2019 Elsevier Ltd. All rights reserved.
引用
收藏
页码：627 / 636
页数：10
相关论文
共 50 条
  • [41] Use of calcium sulfoaluminate cement to improve strength of mortars at low temperature
    Ambroise, J.
    Pera, J.
    CONCRETE REPAIR, REHABILITATION AND RETROFITTING II, 2009, : 325 - 326
  • [42] Effects of calcined phosphogypsum replacement on hydration and properties of calcium sulfoaluminate cement at different curing temperatures
    Liao, Yishun
    Chen, Jiawen
    Yao, Jinxin
    Wang, Kejin
    Huang, Haoran
    Jiang, Guoxi
    Tang, Shengwen
    Zuo, Yibing
    JOURNAL OF SUSTAINABLE CEMENT-BASED MATERIALS, 2025, 14 (04) : 565 - 577
  • [43] Mechanical and Microstructural Characteristics of Calcium Sulfoaluminate Cement Exposed to Early-Age Carbonation Curing
    Wang, Weikang
    Wei, Xuanchun
    Cai, Xinhua
    Deng, Hongyang
    Li, Bokang
    MATERIALS, 2021, 14 (13)
  • [44] EFFECT OF CURING TEMPERATURE ON CEMENT HYDRATION
    Elkhadiri, Imad
    Palacios, Marta
    Puertas, Francisca
    CERAMICS-SILIKATY, 2009, 53 (02) : 65 - 75
  • [45] Effect of calcium sulfoaluminate cement on the hydration process and water resistance of phosphogypsum slag cement
    Tao, Ling
    Deng, Fang
    Xu, Kaiqin
    Dong, Xingzhi
    Xu, Duheng
    Liao, Yishun
    Tang, Shengwen
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2024, 33 : 5375 - 5383
  • [46] Effect of Curing Temperature on Intermediate Temperature Properties of Calcium Aluminate Cement Bonded Corundum Castables
    LI Ye
    LIU Kun
    DING Dafei
    WANG Qingfeng
    FU Xiaohui
    YE Guotian
    China'sRefractories, 2021, 30 (03) : 33 - 36
  • [47] Effect of curing temperature in some hydration characteristics of calcium aluminate cement compared with those of portland cement
    Garces, P
    Alcocel, EG
    Chinchon, S
    Andreu, CG
    Alcaide, J
    CEMENT AND CONCRETE RESEARCH, 1997, 27 (09) : 1343 - 1355
  • [48] Effect of curing temperature and water-to-cement ratio on corrosion of steel in calcium aluminate cement concrete
    Ahmed, Ahmed A.
    Shakouri, Mahmoud
    Trejo, David
    Vaddey, Naga Pavan
    CONSTRUCTION AND BUILDING MATERIALS, 2022, 350
  • [49] Temperature capacitance effect of carbon fibre sulfoaluminate cement composite
    Wang, Shoude
    Lu, Lingchao
    Cheng, Xin
    ADVANCES IN CEMENT RESEARCH, 2012, 24 (06) : 313 - 318
  • [50] Effect of steel slag on the hydration and strength development of calcium sulfoaluminate cement
    Liao, Yishun
    Jiang, Guoxi
    Wang, Kejin
    Al Qunaynah, Siraj
    Yuan, Wenjie
    CONSTRUCTION AND BUILDING MATERIALS, 2020, 265 (265)
12345