Silicon spheroidization treatment of thixoformed Al-Si-Mg alloys

被引:29
|
作者
Ogris, E [1 ]
Lüchinger, H
Uggowitzer, PJ
机构
[1] Swiss Fed Inst Technol, Swiss Fed Inst Technol, Inst Met, CH-8092 Zurich, Switzerland
[2] SAG Aluminium Lend GmbH & Co KG, A-5651 Lend, Austria
[3] THIXALLOY Components GmbH & Co KG, A-5651 Lend, Austria
关键词
silicon; spheroidization; heat treatment; Al-Si-Mg alloy; A356; thixoforming;
D O I
10.4028/www.scientific.net/MSF.396-402.149
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Al-Si-Mg alloys are commonly used in the automobile industry because of their outstanding mechanical properties and corrosion resistance. The need of lighter and safer cars is the driving force behind research in the area of high strength light metal safety part applications. The strength level can be tuned by varying the amount of alloyed magnesium. Usually if strength is increased, ductility will decrease. Following the demands of the automotive industry, safety parts should have a minimum fracture elongation of 15% and a minimum yield strength of 150 MPa. The huge hurdle is the 15% fracture elongation which can not be reached by sand or die casting, but some relatively new alternative casting technologies, like Thixocasting or New Rheocasting, yield encouraging ductility values. Recent research activity has focused on increasing strength and ductility, but so far the results have not yet been satisfying. This paper presents investigations on the spheroidization process of eutectic silicon and its positive effect on mechanical properties. It is shown that the spheroidization process is already finished after minutes of exposure to heat treatment. Metallographical and quantitative microstructural analysis is used to describe the growth and spheroidization process of the silicon crystals. Specimens of THIXALLOY(R)630 (A356) thixocast components were heat treated for varied periods of time, aged and tested. Results show amazing improvements of ductility and strength in comparison to the as cast state. Maximum values of 18% fracture elongation and 230 MPa yield strength are reached.
引用
收藏
页码:149 / 154
页数:6
相关论文
共 50 条
  • [21] Solidification and precipitation behaviour of Al-Si-Mg casting alloys
    Q. G. Wang
    C. J. Davidson
    Journal of Materials Science, 2001, 36 : 739 - 750
  • [22] Effect of SDAS on Homogenization of Al-Si-Mg Casting Alloys
    Zou, Yongzhi
    Xu, Zhengbing
    Zeng, Jianmin
    MANUFACTURING SCIENCE AND ENGINEERING, PTS 1-5, 2010, 97-101 : 1041 - 1044
  • [23] On the strain hardening behaviour of Al-Si-Mg casting alloys
    Wang, QG
    Caceres, CH
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1997, 234 : 106 - 109
  • [24] Fatigue crack growth mechanisms in Al-Si-Mg alloys
    Lados, DA
    SURFACE ENGINEERING, 2004, 20 (06) : 416 - 424
  • [25] Solution Treatment Enhances Both Static and Damping Properties of Al-Si-Mg alloys
    Carneiro, V. H.
    Puga, H.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2018, 49A (12): : 5942 - 5945
  • [26] The effects of Mg amount on the microstructure and mechanical properties of Al-Si-Mg alloys
    Yildirim, Musa
    Ozyurek, Dursun
    MATERIALS & DESIGN, 2013, 51 : 767 - 774
  • [27] Mg effects on the eutectic structure and tensile properties of Al-Si-Mg alloys
    Wang, QG
    Caceres, CH
    ALUMINIUM ALLOYS: THEIR PHYSICAL AND MECHANICAL PROPERTIES, PART 4/SUPPLEMENT, 1997, 242 : 159 - 164
  • [28] The effect of Mg on the microstructure and mechanical behavior of Al-Si-Mg casting alloys
    Caceres, CH
    Davidson, CJ
    Griffiths, JR
    Wang, QG
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1999, 30 (10): : 2611 - 2618
  • [29] Effect of Si content on microstructure and mechanical properties of Al-Si-Mg alloys
    Wang, Yongjin
    Liao, Hengcheng
    Wu, Yuna
    Yang, Jian
    MATERIALS & DESIGN, 2014, 53 : 634 - 638
  • [30] The effect of Mg on the microstructure and mechanical behavior of Al-Si-Mg casting alloys
    C. H. Caceres
    C. J. Davidson
    J. R. Griffiths
    Q. G. Wang
    Metallurgical and Materials Transactions A, 1999, 30 : 2611 - 2618