Pressurized solidification of semi-solid aluminum die casting alloy A356

被引：29
|
作者：
Guo, Hong-Min [1 ]
Yang, Xiang-Jie [1 ]
Wang, Jia-Xuan [2 ]
机构：
[1] Nanchang Univ, Sch Mat Sci & Engn, Nanchang 330031, Jiangxi, Peoples R China
[2] Nanchang Aerosp Univ, Sch Mat Sci & Engn, Nanchang 330063, Peoples R China
来源：
JOURNAL OF ALLOYS AND COMPOUNDS | 2009年 / 485卷 / 1-2期
基金：
中国国家自然科学基金;
关键词：
Metals; Casting; Semi-solid forming; Microstructure; MECHANICAL-PROPERTIES; TENSILE PROPERTIES; MICROSTRUCTURE; MORPHOLOGY;
D O I：
10.1016/j.jallcom.2009.06.083
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
Pressurized solidification behavior of semi-solid aluminum alloy A356 slurry in relation to the final microstructures and mechanical properties has been investigated. Sound semi-solid slurry has been produced, in which the primary alpha-Al presented in average diameter of 65 mu m and shape factor of 0.84. and featured zero-entrapped eutectic. The structural investigation revealed that application of pressure during solidification of semi-solid Slurry could decrease the grain size, improve the morphology of primary alpha-Al and modify the eutectic silicon due to increasing in the cooling rate. Furthermore, higher applied pressures increased the density and improved tensile properties. Subsequent T6 heat treatment raised the mechanical properties of A356 alloy to average values of tensile strength, 330 MPa, yield strength of 240 MPa and elongation of 13%. (C) 2009 Elsevier B.V. All rights reserved
引用
收藏
页码：812 / 816
页数：5
相关论文
共 50 条
  • [31] Defects distribution and control of semi-solid aluminum alloy (A356) parts in thixoforming process
    School of Materials Science and Engineering, Shanghai University, Shanghai 200072, China
    [J]. Tezhong Zhuzao Ji Youse Hejin, 2007, 7 (522-524):
  • [32] Filling ability of semi-solid A356 aluminum alloy slurry in rheo-diecasting
    Bai, Yuelong
    Mao, Weimin
    Gao, Songfu
    Tang, Guoxing
    Xu, Jun
    [J]. JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING, 2008, 15 (01): : 48 - 52
  • [33] Metallurgical structure of A356 aluminum alloy solidified under mechanical vibration: An investigation of alternative semi-solid casting routes
    Limmaneevichitr, Chawalit
    Pongananpanya, Songwid
    Kajornchaiyakul, Julathep
    [J]. MATERIALS & DESIGN, 2009, 30 (09): : 3925 - 3930
  • [34] Filling ability of semi-solid A356 aluminum alloy slurry in rheo-diecasting
    Yuelong Bai~(1
    [J]. International Journal of Minerals,Metallurgy and Materials, 2008, (01) : 48 - 52
  • [35] Preparation of A356 aluminum alloy semi-solid slurry by damper cooling tube method
    School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, China
    不详
    [J]. Tezhong Zhuzao Ji Youse Hejin, 2007, 3 (188-191):
  • [36] Industrial Semi-Solid Rheocasting of Aluminum A356 Brake Calipers
    Curle, U. A.
    Wilkins, J. D.
    Govender, G.
    [J]. ADVANCES IN MATERIALS SCIENCE AND ENGINEERING, 2011, 2011
  • [37] Modeling and optimization of cooling slope process parameters for semi-solid casting of A356 Al alloy
    Khosravi, Hamed
    Eslami-Farsani, Reza
    Askari-Paykani, Mohsen
    [J]. TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2014, 24 (04) : 961 - 968
  • [38] A Compound Process Preparing Semi-Solid A356 Alloy Slurry
    Liu, Zheng
    Mao, Wei Min
    [J]. MANUFACTURING SCIENCE AND ENGINEERING, PTS 1-5, 2010, 97-101 : 1003 - +
  • [39] Effect of yttrium on the microstructure of a semi-solid A356 Al alloy
    Liu Zheng
    Hu Yongmei
    [J]. RARE METALS, 2008, 27 (05) : 536 - 540
  • [40] Study on Thixotropic Property of A356 Alloy in Semi-Solid State
    Simlandi, Sudip
    Barman, Nilkanta
    Chattopadhyay, Himadri
    [J]. SEMI-SOLID PROCESSING OF ALLOYS AND COMPOSITES XII, 2013, 192-193 : 335 - 340
12345