Effect of ZrO2 on sintering characteristics of MgO and MgO-Al2O3 system powder compacts

被引：1
|
作者：
Hashimoto, S
Makita, M
Yamaguchi, A
机构：
[1] Dept. of Mat. Sci. and Engineering, Nagoya Institute of Technology, Showa-ku, Nagoya-shi 466, Gokiso-cho
来源：
JOURNAL OF THE CERAMIC SOCIETY OF JAPAN | 1997年 / 105卷 / 08期
关键词：
zirconium oxide; magnesium oxide; aluminum oxide; relative density; sintering characteristics; microstructure;
D O I：
10.2109/jcersj.105.655
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Effect of ZrO2 on the sintering characteristics of MgO powder compacts was studied. Addition of ZrO2 enhanced the sinterability of the MgO powder compacts and decreased the sintering temperature by about 200 degrees C. When a MgO powder compact with 10 mass% ZrO2 was heated, densification started at 1000 degrees C, and its relative density reached about 98% at 1200 degrees C, Addition of ZrO2 to powder compacts with various ratios of MgO to Al2O3 also increased the sinterability. Particulary, the relative density in compositions containing excess MgO over the equimolar composition of MgO and Al2O3 increased. When a 40 mass% MgO-60 mass% Al2O3 powder compact was heated at 1500 degrees 0 for 2h, the addition of 1 mass% ZrO2 improved the relative density from about 83% of the initial composition to about 97%.
引用
收藏
页码：655 / 659
页数：5
相关论文
共 50 条
  • [31] Preparation of MgO-Al2O3 binary gel system with mesoporous structure
    Kirszensztejn, P
    Przekop, R
    Szymkowiak, A
    Mackowska, E
    Gaca, J
    MICROPOROUS AND MESOPOROUS MATERIALS, 2006, 89 (1-3) : 150 - 157
  • [32] Effect of Spinels on Properties of MgO-Al2O3 Refractories for RH Snorkels
    ZHAO Huizhong
    LI Jingjie
    China'sRefractories, 2021, 30 (03) : 1 - 6
  • [33] ON TETRAHEDRATION OF MGO-AL2O3-ZRO2-SIO2 SYSTEM
    KORDYUK, RA
    GULKO, NV
    DOKLADY AKADEMII NAUK SSSR, 1964, 154 (05): : 1183 - &
  • [34] Effect of Additive ZrO2 on Sintering Properties of MgO-CaO Bricks
    WANG Jiandong1
    China's Refractories, 2007, (01) : 30 - 32
  • [35] Effect of Al2O3 addition on the properties of ZrO2 (2.4 wt% MgO) solid electrolyte
    Wang, Zheng
    Song, Shentai
    Xie, Jun
    Zhong, Qin
    Solid State Ionics, 1988, 28-30 : 508 - 511
  • [36] Sintering and Performance of MgO from Bischofite with ZrO2 Additive
    Huang, Qiongzhu
    Lu, Guimin
    Yu, Jianguo
    MECHANICAL MATERIALS AND MANUFACTURING ENGINEERING III, 2014, 455 : 11 - 17
  • [37] Spark plasma sintering of a-Si3N4 ceramics with MgO-Al2O3 as sintering additives
    Yan, Faqiang
    Chen, Fei
    Shen, Qiang
    Zhang, Lianmeng
    COMPOSITE MATERIALS V, 2007, 351 : 176 - +
  • [38] OXIDATIVE DEHYDROGENATION OF ETHYLBENZENE IN STYRENE ON MgO,ZrO2/Al2O3 CATALYST
    Mammadova, Malahat T.
    PROCESSES OF PETROCHEMISTRY AND OIL REFINING, 2019, 20 (04): : 347 - 355
  • [39] The sintering characteristics of Bi2O3 added MgO-CaO-Al2O3-SiO2 glass powder
    Lo, SH
    Yang, CF
    CERAMICS INTERNATIONAL, 1998, 24 (02) : 139 - 144
  • [40] Effect of addition of TiO2 on reaction sintered MgO-Al2O3 spinels
    Sarkar, R
    Bannerjee, G
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2000, 20 (12) : 2133 - 2141
12345