Microstructure and tribological performance of a dimpled gradient nanoscale TiN layer

被引：20
|
作者：
Zhang, Baosen [1 ,2 ]
Zhu, Shuaishuai [1 ,2 ]
Wang, Zhangzhong [1 ,2 ]
Zhou, Hengzhi [1 ,2 ]
机构：
[1] Nanjing Inst Technol, Sch Mat Engn, Nanjing 211167, Jiangsu, Peoples R China
[2] Jiangsu Key Lab Adv Struct Mat & Applicat Technol, Nanjing 211167, Jiangsu, Peoples R China
来源：
MATERIALS LETTERS | 2016年 / 169卷
基金：
中国国家自然科学基金;
关键词：
Dimpled TiN layer; Gradient nanoscale structure; Multilayer structure; Surfaces; Glow-discharge plasma nitriding; Tribological performance; TITANIUM NITRIDE; COATINGS; DEPOSITION; ALLOY;
D O I：
10.1016/j.matlet.2016.01.085
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The dimpled gradient nanoscale TiN (nano-TiN) layer was prepared on the pure Ti surface by the combined process of supersonic fine particles bombarding (SFPB) and glow-discharge plasma nitriding. A large numbers of dimples (30-40 mu m in diameter) homogenously distribute on the prepared nano-TiN layer surface and are beneficial to the reservation of oil and wear debris during friction process. The nano-TiN layer is about 25 mu m in thickness with a three-layered nanoscale structure and the grain size decreases sequentially from the outer layer to the inner one. The nano-TiN layer with higher mechanical properties displays enhanced friction and wear reducing effects compared to the SFPB-dimpled Ti surface. (C) 2016 Elsevier B.V. All rights reserved.
引用
收藏
页码：214 / 217
页数：4
相关论文
共 50 条
  • [41] Investigation on the tribological performance of functionalized nanoscale silica as an amphiphilic lubricant additive
    Hao, Liang
    Li, Peipei
    Aljabri, A.
    Li, Huaying
    Liu, Guangming
    Xie, Zhongliang
    Li, Tuanjie
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2021, 15 : 5507 - 5515
  • [42] Relation between adsorption and nanoscale tribological performance of organic friction modifiers
    Pham, Alex
    Nalam, Prathima
    Castillo, Veronica
    Thiebaut, Benoit
    Espinosa-Marzal, Rosa
    ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 2017, 253
  • [43] THE TRIBOLOGICAL PROPERTIES AND THE MICROSTRUCTURE INVESTIGATIONS OF TIN BABBIT WITH Pb ADDITION AFTER HEAT TREATMENT
    Leszczynska-Madej, B.
    Madej, M.
    ARCHIVES OF METALLURGY AND MATERIALS, 2016, 61 (04) : 1861 - 1867
  • [44] Influence of carbon content on the microstructure and tribological properties of TiN(C) coatings in water lubrication
    Wang, Qianzhi
    Zhou, Fei
    Zhou, Zhifeng
    Yang, Yang
    Yan, Ce
    Wang, Chundong
    Zhang, Wenjun
    Li, Lawrence Kwok-Yan
    Bello, Igor
    Lee, Shui-Tong
    SURFACE & COATINGS TECHNOLOGY, 2012, 206 (18): : 3777 - 3787
  • [45] MICROSTRUCTURE AND TRIBOLOGICAL PROPERTIES OF TIN BRONZE-GRAPHITE COMPOSITES MADE BY STIR CASTING
    Kulasa, J.
    Malec, W.
    Juszczyk, B.
    Malara, S.
    Cwolek, B.
    METALURGIJA, 2016, 55 (01): : 19 - 21
  • [46] The microstructure, mechanical and tribological properties of TiN coatings after Nb and C ion implantation
    Deng, Bin
    Tao, Ye
    Hu, Zhijie
    APPLIED SURFACE SCIENCE, 2013, 284 : 405 - 411
  • [47] Microstructure and wear performance of gradient Ti/TiN metal matrix composite coating synthesized using a gas nitriding technology
    Cui, ZD
    Zhu, SL
    Man, HC
    Yang, XJ
    SURFACE & COATINGS TECHNOLOGY, 2005, 190 (2-3): : 309 - 313
  • [48] Enhancement of Biocompatibility of Metal Implants by Nanoscale TiN/NbN Multi layer Coatings
    Subramanian, B.
    JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY, 2013, 13 (07) : 4565 - 4572
  • [49] FATIGUE PERFORMANCE AND TRIBOLOGICAL PROPERTIES OF RF-SPUTTERED TIN COATINGS
    HERR, W
    MATTHES, B
    BROSZEIT, E
    KLOOS, KH
    SURFACE & COATINGS TECHNOLOGY, 1993, 57 (01): : 43 - 46
  • [50] Tribological performance evaluation of (111) preferred oriented TiN duplex coatings
    Ishii, Junya
    Haruyama, Yoshio
    Kawamura, Shingo
    Horikawa, Noriyo
    Iwai, Yoshiro
    WEAR, 2009, 267 (12) : 2173 - 2178
12345