Fabrication of Bi-2212 Films on Ag Substrate by Dip-coating Method

被引：2
|
作者：
Xu, Jie [1 ]
Li, Mingya [1 ]
Wang, Xiaoyan [1 ]
机构：
[1] Northeastern Univ, Dept Mat Sci & Engn, Qinhuangdao 066004, Hebei Province, Peoples R China
来源：
HIGH-PERFORMANCE CERAMICS VII, PTS 1 AND 2 | 2012年 / 512-515卷
关键词：
Bi-2212; film; Ag substrate; Dip-coating method; THICK-FILMS;
D O I：
10.4028/www.scientific.net/KEM.512-515.360
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
In this study, Bi2Sr2CaCu2Ox (Bi-2212) thick films on Ag substrate were fabricated using the dip-coating method. The phase compositions of the samples were characterized using the XRD. The microstructure was observed using SEM. Experimental results show that the temperature of heat treatment strongly influence the phase formation of Bi-2212. The Bi-2212 film fabricated with powder calcined at 800 degrees C has compact surface and textured structure when heat treated at 830 degrees C.
引用
收藏
页码：360 / 363
页数：4
相关论文
共 50 条
  • [1] The preparation and characterization of Bi-2212 film on Ag substrate by dip-coating method
    Song, Yang
    Zhao, Liang
    Li, Pei
    Qu, Timing
    Huang, Yong
    Han, Zhenghe
    [J]. PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2006, 442 (02): : 134 - 138
  • [2] Performance tests of Bi-2212 insert magnets fabricated by Ag sheath method and dip-coating method
    Kumakura, H
    Kitaguchi, H
    Kiyoshi, T
    Inoue, K
    Togano, K
    Okada, M
    Fukushima, K
    Tanaka, K
    Kato, K
    Sato, J
    [J]. IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 1997, 7 (02) : 646 - 649
  • [3] BI-2212 OXIDE SUPERCONDUCTING TAPES AND COILS BY DOCTOR-BLADE-CASTING AND DIP-COATING PROCESSES
    MAEDA, H
    TOGANO, K
    KUMAKURA, H
    [J]. CHINESE JOURNAL OF PHYSICS, 1992, 30 (02) : 217 - 227
  • [4] Structures and superconducting properties of Bi-2212 oxide cylinders prepared by the dip-coating and subsequent diffusion reaction
    Yamada, Y
    Itoh, K
    Wada, K
    Tachikawa, K
    [J]. IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 1999, 9 (02) : 1868 - 1871
  • [5] Fabrication of laminated Bi-2212/Ag multifilamentary tape
    Yuan, DW
    Majer, WJ
    Francavilla, TL
    [J]. SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2000, 13 (03): : 287 - 290
  • [6] Processing Bi-2212/Ag thick films under a high magnetic field: on the Bi-2212/Ag interface effect
    Liu, HB
    Ferreira, PJ
    Vander Sande, JB
    [J]. PHYSICA C, 1998, 303 (3-4): : 161 - 168
  • [7] Fabrication of Uniformly Growing Graphene Films via the Dip-coating Method
    Yang Juan
    Sun Hong-bo
    Li Dan
    [J]. CHINA FUNCTIONAL MATERIALS TECHNOLOGY AND INDUSTRY FORUM, 2013, 320 : 185 - 189
  • [8] Formation processes of Bi-2212 films prepared on Ag(001) substrate by an atomization technique
    Su, Y
    Satoh, Y
    Arisawa, S
    Takano, Y
    Ishii, A
    Hatano, T
    Togano, K
    [J]. PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2002, 372 : 619 - 622
  • [9] Fabrication and properties of superconducting AgNiMg and Ag/Bi-2212 wires
    Wesche, R
    Fuchs, AM
    Pasztor, G
    [J]. HIGH TEMPERATURE SUPERCONDUCTORS: SYNTHESIS, PROCESSING, AND LARGE-SCALE APPLICATIONS, 1996, : 157 - 166
  • [10] Fabrication of Bi-2212 superconductor using Ag/Ni clad tape as low cost substrate
    Nemoto, Y
    Miao, H
    Fujii, H
    Kitaguchi, H
    Kumakura, H
    Togano, K
    Shima, K
    [J]. PHYSICA C, 2000, 339 (03): : 209 - 213
12345